The aim of this study was to compare three pretreatments (grinding, grinding + sodium hydroxide + 1%, and grinding + hydrothermal process) applied to peel ripe bananas (substrate) and its effect on the production of dextrose syrup by enzymatic hydrolysis the fungus Trichoderma ressei. Twenty seven cultures were prepared in different concentrations peel ripe bananas (40%, 50% and 60%) , factor A, subject to the three afore mentioned pretreatments , factor B. The biomass obtained was inoculated with conidia of the fungus Trichoderma ressei in a concentration of 0.2 ; 0.4 and 0.6 g/L , factor C, giving a 3x3x3 factorial experiment . Additionally, variation in these factors in time (four factors) was valued. Six days (144 hours) incubation at pH 4.2 - 5was performed at room temperature. The glucose concentration in the hydrolyzate was measured using the DNS method (di nitrosalisílic acid) i...

This research addresses the application of compound polyethylene glycol (PEG) of molecular weight 1500, whose objective is to degrade the inhibiting compounds present during the enzymatic hydrolysis of Cavendish variety ripe banana peels. Likewise, three experiments were conducted on 60% ground banana peel, to which PEG was added at different concentrations: 0.01; 0.02; and 0.03 g/g biomass. The enzymatic hydrolysis was performed with conidia of the Trichoderma viride fungus and its subsequent alcoholic fermentation with commercial active dry yeast Saccharomyces cerevisiae, which was previously activated. The best result corresponds to the PEG3 experiment (0.03 g/g biomass), with which a greater increase of reducing sugars was obtained. In addition, significant differences were found (p<0.5) in the glucose obtained among the three hydrolytic treatments. The results show that bioethano...

El objetivo de la presente investigación fue comparar tres pre tratamientos (molienda; molienda + hidróxido de sodio al 1%, y molienda + proceso hidrotérmico) aplicados a cáscara de banano maduro (sustrato) y su efecto en la obtención de jarabe glucosado mediante hidrólisis enzimática con el hongo Trichoderma ressei. Se prepararon 27 medios de cultivos en diferentes concentraciones de cáscara de banano maduro (40%, 50% y 60%), factor A; sometidas a los tres pretratamientos antes señalados, factor B. La biomasa obtenida fue inoculada con conidias del hongo Trichoderma ressei en una concentración de 0,2; 0,4 y 0,6 g/L, factor C, dando un experimento factorial 3x3x3. Adicionalmente, se evaluó la variación de estos factores en el tiempo (cuatro factores). Se realizó la incubación por 144 horas a temperatura ambiente y pH 4,2-5. Se midió la concentración de glucosa presente en...

Esta investigación aborda la aplicación de un compuesto de polietilenglicol (PEG) de masa molecular 1500, cuyo objetivo es degradar los compuestos inhibidores presentes durante la hidrólisis enzimática de la cáscara de banano maduro de la variedad Cavendish. Asimismo, se realizaron tres experimentos al 60% de cáscara de banano molida, en los que se adicionó PEG a diferentes concentraciones: 0,01; 0,02; 0,03 g/g biomasa. La hidrólisis enzimática se realizó con conidios del hongo Trichoderma viride y su posterior fermentación alcohólica fue con levadura activa seca comercial de Saccharomyces cerevisiae, que previamente fue activada. El mejor resultado corresponde al experimento PEG3 (0,03 g/g biomasa), con el que se obtuvo un mayor incremento de azúcares reductores. Además, se encontraron diferencias significativas (p<0,5) para la glucosa obtenida entre los tres tratamient...

Water contaminated by heavy metals is a risk to public health. This is the reason behind widespread research on water treatment oriented to removing metal ions. This research determined the intensity of adsorption of lead (Pb) by the Azolla caroliniana fern and its capacity to remove lead in synthetic waters. An atomic absorption spectrophotometer was used to determine the concentration of adsorbed lead. Langmuir isotherm graphs showed that the type of isothermal system was unfavorable for the four reactors used in the study (RL's greater than 1). On the other hand, Freundlich isotherm graphs showed the linear models of the kinetic behavior of lead adsorption by Azolla caroliniana for the four reactors and enabled us to determine that the best R2 and the highest adsorption intensity (n) of Pb (0,122) was achieved with reactor D (30 ppm Pb).

Water contaminated by heavy metals is a risk to public health. This is the reason behind widespread research on water treatment oriented to removing metal ions. This research determined the intensity of adsorption of lead (Pb) by the Azolla caroliniana fern and its capacity to remove lead in synthetic waters. An atomic absorption spectrophotometer was used to determine the concentration of adsorbed lead. Langmuir isotherm graphs showed that the type of isothermal system was unfavorable for the four reactors used in the study (RL's greater than 1). On the other hand, Freundlich isotherm graphs showed the linear models of the kinetic behavior of lead adsorption by Azolla caroliniana for the four reactors and enabled us to determine that the best R2 and the highest adsorption intensity (n) of Pb (0,122) was achieved with reactor D (30 ppm Pb).

The objective of this research was to determine corrosion rate (Vcorr) iron ASTM A36, in solutions of sodiumx cyanide and thiourea. Further evaluate the effect of this electrochemical phenomenon in costs associated with gold leaching processes. The corrosion rate was determined in mm / year by polarization curves. Costs were determined by a cost analysis using synthetic indicators. The corrosion rate of iron ASTM A36 in sodium cyanide solutions in concentrations of 0.62 g / L; 0.80 g / L and thiourea solutions 0.96 g / L; 1.24 g / L was evaluated. The results show that the corrosion rate of the metal is slightly higher in the solution of thiourea 1.24 g / L (3.03 mm / year) with the following behavior: Thiourea 1.24g / L> Thiourea 0.96 g / L> Cyanide 0.80 g / L ≈ Cyanide 0.62 g / L. It was estimated that corrosion costs in gold leaching processes are between 4.78 and 5.20% of the...

En esta investigación se determinó la velocidad de corrosión (Vcorr) de hierro ASTM A36, en soluciones de cianuro de sodio en concentraciones de 0,62 g/L; 0,80 g/L y de tiourea 0.96 g/L; 1.24 g/L. Adicionalmente se evaluó el efecto de este deterioro en los costos asociados a procesos de lixiviación aurífera. La velocidad de corrosión se determinó en mm/año mediante curvas de polarización. Se realizó un análisis de costos utilizando indicadores sintéticos. Los resultados muestran que la velocidad de corrosión del metal es ligeramente mayor en la solución de tiourea 1,24 g/L (3,03 mm/año) con el siguiente comportamiento: corrosión de hierro ASTM A36 en Tiourea 1,24g/L > Tiourea 0,96 g/L > Cianuro 0,80 g/L ≈ Cianuro 0,62 g/L. Se pudo estimar que los costos por corrosión en los procesos de lixiviación aurífera se encuentran entre el 4,78 y 5,20% del capital para c...

The objective of this work was to determine cadmium ultratraces using voltammetric techniques, whit a vitreous carbon electrode modified with bismuth film (BiFE). in situ with Eprec=-1,2V and a deposition time of tprec= 100s in the medium of sodium acetate/acetic acid 0,1M (pH 4,5) in the absence of oxygen, using linear scan voltammetry(LSV) whit concentrations of 100-800 μg.L-1 and 2-10mg.L-1 and square wave voltammetry(SWV) whit concentrations of 50-800μg.L-1. Were obtained voltamograms of potential vs intensity of the current and graphs of concentration vs intensity of the current, whit linearities of 0,997, 0,992 and 0,997 respectively. Was observed better sensitivity in SWV observing more pronounced peaks for both cadmium and bismuth, reaching the potential of oxidation of cadmium for LSV -0,701V, -0,68V and SWV in -0,701V.

Se validó un método voltamétrico para determinar la concentración de antimonio en medio acuoso. Se usó la técnica voltamperométrica de redisolución anódica, utilizando un potenciostato. Se aplicó cronoamperometría a E= -1,2 V durante 50 s. Se aplicó una voltametría de barrido lineal con potenciales entre Ei = -1,2 V y Ef = 0,5 V a una velocidad de 20 mV/s. Esto se llevó a cabo en solución electrolítica H3 PO4 0,5 M, donde se puede observar un incremento en el pico de intensidad de corriente en función de la concentración de las soluciones evaluadas a un potencial de 84,96 mV. Para validar el método se determinó la linealidad, precisión, límite de detección y límite de cuantificación. Se prepararon cuatro concentraciones de antimonio por triplicado, en un rango de 1, 5, 10, 15, 20 mg/L, respectivamente. Se construyó una curva de calibración de concentración exp...

The objective of this research was to demonstrate the effectiveness of polyurethane paints for the protection against corrosion of galvanized steel. The methodology consisted of performing electrochemical analysis by means of polarization curves and accelerated corrosion tests (salt spray chamber) of the behavior of the duplex and galvanized protection systems in 3.5% NaCl. In addition, the SEM analysis (scanning electron microscopy) was carried out with an EDAX analysis (X-ray spectroscopy of dispersive energy) observing the morphology and the composition of the corrosion products. According to the polarization curves, there are differences in each galvanized and duplex system in the studied medium. The duplex systems have a more positive corrosion potential than the potentials of the galvanized steel samples in the salt fog chamber (-950mv, -1070mv of duplex steel and -1065mv, 1080mv o...

El objetivo de esta investigación fue demostrar la efectividad de las pinturas de poliuretano para la protección contra la corrosión del acero galvanizado. La metodología consistió en realizar análisis electroquímico mediante curvas de polarización y pruebas de corrosión acelerada (cámara de niebla salina) del comportamiento de los sistemas de protección dúplex y galvanizado en NaCl al 3,5%. Además, el análisis MEB (microscopía electrónica de barrido) se llevó a cabo con un análisis EDAX (espectroscopia de rayos X de energía dispersiva) observando la morfología y la composición de los productos de corrosión. Según las curvas de polarización, hay diferencias en cada sistema galvanizado y dúplex en el medio estudiado. Los sistemas dúplex tienen un potencial de corrosión más positivo que los potenciales de las muestras de acero galvanizado en cámara de niebla sa...