The objective of this research was to determine corrosion rate (Vcorr) iron ASTM A36, in solutions of sodiumx cyanide and thiourea. Further evaluate the effect of this electrochemical phenomenon in costs associated with gold leaching processes. The corrosion rate was determined in mm / year by polarization curves. Costs were determined by a cost analysis using synthetic indicators. The corrosion rate of iron ASTM A36 in sodium cyanide solutions in concentrations of 0.62 g / L; 0.80 g / L and thiourea solutions 0.96 g / L; 1.24 g / L was evaluated. The results show that the corrosion rate of the metal is slightly higher in the solution of thiourea 1.24 g / L (3.03 mm / year) with the following behavior: Thiourea 1.24g / L> Thiourea 0.96 g / L> Cyanide 0.80 g / L ≈ Cyanide 0.62 g / L. It was estimated that corrosion costs in gold leaching processes are between 4.78 and 5.20% of the...

En esta investigación se determinó la velocidad de corrosión (Vcorr) de hierro ASTM A36, en soluciones de cianuro de sodio en concentraciones de 0,62 g/L; 0,80 g/L y de tiourea 0.96 g/L; 1.24 g/L. Adicionalmente se evaluó el efecto de este deterioro en los costos asociados a procesos de lixiviación aurífera. La velocidad de corrosión se determinó en mm/año mediante curvas de polarización. Se realizó un análisis de costos utilizando indicadores sintéticos. Los resultados muestran que la velocidad de corrosión del metal es ligeramente mayor en la solución de tiourea 1,24 g/L (3,03 mm/año) con el siguiente comportamiento: corrosión de hierro ASTM A36 en Tiourea 1,24g/L > Tiourea 0,96 g/L > Cianuro 0,80 g/L ≈ Cianuro 0,62 g/L. Se pudo estimar que los costos por corrosión en los procesos de lixiviación aurífera se encuentran entre el 4,78 y 5,20% del capital para c...

The objective of this work was to determine cadmium ultratraces using voltammetric techniques, whit a vitreous carbon electrode modified with bismuth film (BiFE). in situ with Eprec=-1,2V and a deposition time of tprec= 100s in the medium of sodium acetate/acetic acid 0,1M (pH 4,5) in the absence of oxygen, using linear scan voltammetry(LSV) whit concentrations of 100-800 μg.L-1 and 2-10mg.L-1 and square wave voltammetry(SWV) whit concentrations of 50-800μg.L-1. Were obtained voltamograms of potential vs intensity of the current and graphs of concentration vs intensity of the current, whit linearities of 0,997, 0,992 and 0,997 respectively. Was observed better sensitivity in SWV observing more pronounced peaks for both cadmium and bismuth, reaching the potential of oxidation of cadmium for LSV -0,701V, -0,68V and SWV in -0,701V.

Se validó un método voltamétrico para determinar la concentración de antimonio en medio acuoso. Se usó la técnica voltamperométrica de redisolución anódica, utilizando un potenciostato. Se aplicó cronoamperometría a E= -1,2 V durante 50 s. Se aplicó una voltametría de barrido lineal con potenciales entre Ei = -1,2 V y Ef = 0,5 V a una velocidad de 20 mV/s. Esto se llevó a cabo en solución electrolítica H3 PO4 0,5 M, donde se puede observar un incremento en el pico de intensidad de corriente en función de la concentración de las soluciones evaluadas a un potencial de 84,96 mV. Para validar el método se determinó la linealidad, precisión, límite de detección y límite de cuantificación. Se prepararon cuatro concentraciones de antimonio por triplicado, en un rango de 1, 5, 10, 15, 20 mg/L, respectivamente. Se construyó una curva de calibración de concentración exp...