After fabricating five metallographic specimens of the Cu0.95Al0.05 alloy from electrolytic copper and aluminum, these ones were both microstructurally characterized by using a metallographic optical microscope at room temperature and subjected to mechanical traction in order to chart the stress-strain curve. From the characterization, it has been found out that the Cu0.95Al0.05 microstructure is composed of a single phase, and from the tensile tests, it has been obtained its rupture point, 249.361 MPa. The obtained results were explained in the framework of the theory of metals and metal alloys.

Las aguas servidas de uso doméstico representan el principal factor que contaminan los ecosistemas del Lago Titicaca ubicado en Perú y Bolivia. Por ello, la Universidad Alas Peruanas-Perú, ha generado investigación aprobada por Resolución No 102-2018-VIeIT-UAP, cuyo objetivo general es contribuir con propuestas de mejoras en la operatividad de las Plantas de Tratamiento de Aguas Residuales Domésticas (PTARD) que permitan reducir la contaminación de las aguas del lago Titicaca-Sector Perú; investigación que fue presentada en la Conferencia de Innovación IWA-BID sobre Uso Sostenible del Agua; Ciudades, industria y agricultura, realizada en la Ciudad de Guayaquil-Ecuador en el mes de octubre 2019.En la investigación se elaboró diagnóstico del estado situacional de 16 sistemas de tratamientos de aguas residuales domésticas ubicadas alrededor del Lago y alternativas de mejoras p...