One-dimensional nanostructures have shown high photocatalytic efficiency due to their high surface area to volume ratio and charge transfer efficiency. In this work, we have studied the influence of zinc acetate content (zinc acetate to polyvinyl alcohol (PVA) mass ratio) on the photoelectrochemical performance of zinc oxide (ZnO) nanostructures. The nanostructures of ZnO were fabricated on fluorine-doped tin oxide glass substrate by electrospinning of aqueous solution containing different amounts of zinc acetate. The precursor nanofibers of zinc acetate/PVA were converted into polycrystalline ZnO nanostructures with hexagonal wurtzite crystal structure by calcination at 600°C for 3 h. It was found that by increasing the amount of zinc acetate, the diameter of the as-spun precursor fibers increased and their distribution became broader. The mean diameter of the ZnO nanoparticles forming...

ZnO/TiO2 nanostructures were fabricated by an electrostatically modified electrospinning technique using zinc acetate and commercially available TiO2-P25, polyvinyl alcohol, and a solvent. It was found that the TiO2-P25 nanoparticles were attached to the ZnO nanostructures, and the mean diameter of the nanoparticles forming the nanostructures ranged from 31 to 52 nm with increasing the amount of zinc acetate. The obtained results evidenced that the coupling of TiO2 with ZnO enhanced the IPCE and improved the photocatalytic activity of ZnO. Particularly, the ZnO/TiO2 nanostructures fabricated with a zinc acetate-to-PVA ratio of 2:3 exhibited the highest IPCE and photocatalytic activity.