The following article presents the results of performance evaluation systems anticorrosive paint for use in the national industry, epoxy systems, using the accelerated salt spray (fog) test(ASTM B 117). The experiment was carried out for a period of exposure 125 days or 3000hours. The paint systems were tested applied on steel plates with different types of surfacepreparation: manual, mechanical and sandblasted (white, dry and wet). The evaluation ofthe samples tested were made according to the criteria of the relevant standards: Grade Oxidation, Blistering and Deterioration in Incision. The degree of deterioration in the incision showed that the epoxy systems with sandblasting surface preparation show a greater resistance to deterioration in the incision, compared to those of surface preparation manual cleaning and mechanical cleaning.

En el siguiente artículo se presenta los resultados obtenidos de 1a evaluación del comportamiento anticorrosivo de sistemas de pinturas de uso en la industria nacional, sistemas epóxicos; utilizando el ensayo acelerado de niebla salina (ASTM B 117). El ensayo se realizó por un período de exposición de 125 días ó 3000 horas. Los sistemas de pinturas ensayados fueron aplicados sobre placas de acero con diferentes tipos de preparación de superficie: manual, mecánico y arenado (al blanco, en seco y en húmedo). La evaluación de las muestras ensayadas se realizó según los criterios de las normas correspondientes: Grado de Oxidación, Ampollamiento y Deterioro en la Incisión. El grado de deterioro en la incisión permitió observar que los sistemas epóxicos con preparación de superficie de arenado muestran una mayor resistencia al deterioro en la incisión, comparados con los d...