"Influencia de la temperatura y la agitación del medio corrosivo constituido por h2so4-0.5 m y hcl-0.5 m, sobre la velocidad de corrosión del acero astm a192, medido mediante diferentes técnicas electroquímicas”

Descripción del Articulo

ASTM A192 is widely employed for boiler tubing and steam piping in thermal power plants. Scale formation in internal surface of boiler tubes is one of the major problems in most of high-pressure boilers of thermal power stations. Two major problems result from deposit fouling on the interior tube su...

Descripción completa

Detalles Bibliográficos
Autores: Lezama Vergara, Gary Cristhian, Loyola Rodriguez, Manuel Fernando
Formato: tesis de grado
Fecha de Publicación:2014
Institución:Universidad Nacional de Trujillo
Repositorio:UNITRU-Tesis
Lenguaje:español
OAI Identifier:oai:dspace.unitru.edu.pe:20.500.14414/10391
Enlace del recurso:https://hdl.handle.net/20.500.14414/10391
Nivel de acceso:acceso abierto
Materia:Agitación del medio corrosivo
id UNIT_0924c80bffdb17c0ea1842e5ea65e151
oai_identifier_str oai:dspace.unitru.edu.pe:20.500.14414/10391
network_acronym_str UNIT
network_name_str UNITRU-Tesis
repository_id_str 4801
dc.title.es_PE.fl_str_mv "Influencia de la temperatura y la agitación del medio corrosivo constituido por h2so4-0.5 m y hcl-0.5 m, sobre la velocidad de corrosión del acero astm a192, medido mediante diferentes técnicas electroquímicas”
title "Influencia de la temperatura y la agitación del medio corrosivo constituido por h2so4-0.5 m y hcl-0.5 m, sobre la velocidad de corrosión del acero astm a192, medido mediante diferentes técnicas electroquímicas”
spellingShingle "Influencia de la temperatura y la agitación del medio corrosivo constituido por h2so4-0.5 m y hcl-0.5 m, sobre la velocidad de corrosión del acero astm a192, medido mediante diferentes técnicas electroquímicas”
Lezama Vergara, Gary Cristhian
Agitación del medio corrosivo
title_short "Influencia de la temperatura y la agitación del medio corrosivo constituido por h2so4-0.5 m y hcl-0.5 m, sobre la velocidad de corrosión del acero astm a192, medido mediante diferentes técnicas electroquímicas”
title_full "Influencia de la temperatura y la agitación del medio corrosivo constituido por h2so4-0.5 m y hcl-0.5 m, sobre la velocidad de corrosión del acero astm a192, medido mediante diferentes técnicas electroquímicas”
title_fullStr "Influencia de la temperatura y la agitación del medio corrosivo constituido por h2so4-0.5 m y hcl-0.5 m, sobre la velocidad de corrosión del acero astm a192, medido mediante diferentes técnicas electroquímicas”
title_full_unstemmed "Influencia de la temperatura y la agitación del medio corrosivo constituido por h2so4-0.5 m y hcl-0.5 m, sobre la velocidad de corrosión del acero astm a192, medido mediante diferentes técnicas electroquímicas”
title_sort "Influencia de la temperatura y la agitación del medio corrosivo constituido por h2so4-0.5 m y hcl-0.5 m, sobre la velocidad de corrosión del acero astm a192, medido mediante diferentes técnicas electroquímicas”
author Lezama Vergara, Gary Cristhian
author_facet Lezama Vergara, Gary Cristhian
Loyola Rodriguez, Manuel Fernando
author_role author
author2 Loyola Rodriguez, Manuel Fernando
author2_role author
dc.contributor.advisor.fl_str_mv Zavaleta Gutierrez, Nilthon Emerson
dc.contributor.author.fl_str_mv Lezama Vergara, Gary Cristhian
Loyola Rodriguez, Manuel Fernando
dc.subject.es_PE.fl_str_mv Agitación del medio corrosivo
topic Agitación del medio corrosivo
description ASTM A192 is widely employed for boiler tubing and steam piping in thermal power plants. Scale formation in internal surface of boiler tubes is one of the major problems in most of high-pressure boilers of thermal power stations. Two major problems result from deposit fouling on the interior tube surface: (1) Loss of heat transfer, and (2) Under-deposit corrosion. Therefore, it is necessary to clean, and mineral acids are typically employed for this purpose. The present study addresses the corrosion behavior of ASTM A192 steel in hydrochloric and sulfuric acid solution at different temperature and agitation using different technique electrochemical. The relationship between the rate of corrosion on ASTM A192 steel and the temperature of the acid medium follows the Arrhenius kinetic model. The increase of the temperature and agitation of the acid medium produced on the surface of the ASTM A192 steel a depolarization of the reaction of hydrogen evolution, which contributes to the increase in the rate of corrosion. Also, the corrosion rate in HCl-0.5M is slightly greater than in H2SO4-0.5M, therefore, the acid cleaning process for boiler components made of ASTM A192 steel will be satisfactory, when performed in any of the evaluated media without stirring (method of filling and soaked) and at temperature up to 65 oC
publishDate 2014
dc.date.accessioned.none.fl_str_mv 2018-06-28T15:03:02Z
dc.date.available.none.fl_str_mv 2018-06-28T15:03:02Z
dc.date.issued.fl_str_mv 2014-01
dc.type.es_PE.fl_str_mv info:eu-repo/semantics/bachelorThesis
format bachelorThesis
dc.identifier.uri.none.fl_str_mv https://hdl.handle.net/20.500.14414/10391
url https://hdl.handle.net/20.500.14414/10391
dc.language.iso.es_PE.fl_str_mv spa
language spa
dc.relation.ispartof.fl_str_mv SUNEDU
dc.relation.ispartofseries.none.fl_str_mv Tmt;Tmt
dc.rights.es_PE.fl_str_mv info:eu-repo/semantics/openAccess
dc.rights.uri.es_PE.fl_str_mv http://creativecommons.org/licenses/by-nc-nd/2.5/pe/
eu_rights_str_mv openAccess
rights_invalid_str_mv http://creativecommons.org/licenses/by-nc-nd/2.5/pe/
dc.publisher.es_PE.fl_str_mv Universidad Nacional de Trujillo
dc.source.es_PE.fl_str_mv Universidad Nacional de Trujillo
Repositorio institucional - UNITRU
dc.source.none.fl_str_mv reponame:UNITRU-Tesis
instname:Universidad Nacional de Trujillo
instacron:UNITRU
instname_str Universidad Nacional de Trujillo
instacron_str UNITRU
institution UNITRU
reponame_str UNITRU-Tesis
collection UNITRU-Tesis
bitstream.url.fl_str_mv https://dspace.unitru.edu.pe/bitstreams/2836407d-3174-48c3-a691-f7fa520feb7f/download
https://dspace.unitru.edu.pe/bitstreams/65b8a20c-921f-40d7-b81b-1c0823d8faa0/download
bitstream.checksum.fl_str_mv 448eaae46aeaea57cb1fb9b3a69958a3
8a4605be74aa9ea9d79846c1fba20a33
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
repository.name.fl_str_mv Repositorio Institucional - UNITRU
repository.mail.fl_str_mv repositorios@unitru.edu.pe
_version_ 1807290163657703424
spelling Zavaleta Gutierrez, Nilthon EmersonLezama Vergara, Gary CristhianLoyola Rodriguez, Manuel Fernando2018-06-28T15:03:02Z2018-06-28T15:03:02Z2014-01https://hdl.handle.net/20.500.14414/10391ASTM A192 is widely employed for boiler tubing and steam piping in thermal power plants. Scale formation in internal surface of boiler tubes is one of the major problems in most of high-pressure boilers of thermal power stations. Two major problems result from deposit fouling on the interior tube surface: (1) Loss of heat transfer, and (2) Under-deposit corrosion. Therefore, it is necessary to clean, and mineral acids are typically employed for this purpose. The present study addresses the corrosion behavior of ASTM A192 steel in hydrochloric and sulfuric acid solution at different temperature and agitation using different technique electrochemical. The relationship between the rate of corrosion on ASTM A192 steel and the temperature of the acid medium follows the Arrhenius kinetic model. The increase of the temperature and agitation of the acid medium produced on the surface of the ASTM A192 steel a depolarization of the reaction of hydrogen evolution, which contributes to the increase in the rate of corrosion. Also, the corrosion rate in HCl-0.5M is slightly greater than in H2SO4-0.5M, therefore, the acid cleaning process for boiler components made of ASTM A192 steel will be satisfactory, when performed in any of the evaluated media without stirring (method of filling and soaked) and at temperature up to 65 oCEl acero ASTM A192 es ampliamente utilizado en tuberías de calderas y tubos de vapor en las centrales térmicas. La formación de incrustaciones en la superficie interna de los tubos de la caldera es uno de los problemas más importantes en la mayoría de las calderas de alta presión de las centrales térmicas. Dos problemas importantes resultan desde los sedimentos en la superficie interior del tubo: (1) La pérdida de transferencia de calor, y (2) la corrosión debajo de estos depósitos. Por lo tanto, es necesario limpiarlos y los ácidos minerales son típicamente empleados para este fin. El presente estudio aborda el comportamiento a la corrosión del acero ASTM A192 en ácido clorhídrico y ácido sulfúrico a distinta temperatura y agitación, utilizando diferentes técnicas electroquímicas. La relación entre la velocidad de corrosión de acero A192 y la temperatura del medio ácido sigue el modelo cinético de Arrhenius. El incremento de la temperatura y agitación del medio ácido produce en la superficie del acero ASTM A192 una despolarización de la reacción de evolución de hidrógeno, lo que contribuye al incremento de su velocidad de corrosión. Asimismo, la velocidad de corrosión en HCl-0.5M es ligeramente mayor que en H2SO4-0.5M, por lo que, el proceso de limpieza ácida para componentes de la caldera fabricadas con acero ASTM A192 serán satisfactorias, si se realiza en cualquiera de los medios evaluados sin agitación (método de llenado y remojado) y a temperaturas hasta 65 ºCTesisspaUniversidad Nacional de TrujilloTmt;TmtSUNEDUinfo:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by-nc-nd/2.5/pe/Universidad Nacional de TrujilloRepositorio institucional - UNITRUreponame:UNITRU-Tesisinstname:Universidad Nacional de Trujilloinstacron:UNITRUAgitación del medio corrosivo"Influencia de la temperatura y la agitación del medio corrosivo constituido por h2so4-0.5 m y hcl-0.5 m, sobre la velocidad de corrosión del acero astm a192, medido mediante diferentes técnicas electroquímicas”info:eu-repo/semantics/bachelorThesisTítulo ProfesionalIngeniero MetalúrgicoIngenieríaUniversidad Nacional de Trujillo. Facultad de IngenieríaORIGINALLezama Vergara - Loyola Rodriguez.pdfLezama Vergara - Loyola Rodriguez.pdfAgitacion del medio corrosivoapplication/pdf8537900https://dspace.unitru.edu.pe/bitstreams/2836407d-3174-48c3-a691-f7fa520feb7f/download448eaae46aeaea57cb1fb9b3a69958a3MD51LICENSElicense.txtlicense.txttext/plain; charset=utf-81748https://dspace.unitru.edu.pe/bitstreams/65b8a20c-921f-40d7-b81b-1c0823d8faa0/download8a4605be74aa9ea9d79846c1fba20a33MD5220.500.14414/10391oai:dspace.unitru.edu.pe:20.500.14414/103912018-06-28 10:03:02.912http://creativecommons.org/licenses/by-nc-nd/2.5/pe/info:eu-repo/semantics/openAccessopen.accesshttps://dspace.unitru.edu.peRepositorio Institucional - UNITRUrepositorios@unitru.edu.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
score 13.962467
"Influencia de la temperatura y la agitación del medio corrosivo constituido por h2so4-0.5 m y hcl-0.5 m, sobre la velocidad de corrosión del acero astm a192, medido mediante diferentes técnicas electroquímicas”
Nota importante:
La información contenida en este registro es de entera responsabilidad de la institución que gestiona el repositorio institucional donde esta contenido este documento o set de datos. El CONCYTEC no se hace responsable por los contenidos (publicaciones y/o datos) accesibles a través del Repositorio Nacional Digital de Ciencia, Tecnología e Innovación de Acceso Abierto (ALICIA).

Ejemplares Similares