Objectives: Compare the impact of an aerated beverage on the surface microhardness of three nanofilled composite resins (Filtek Z250 XT, Filtek Z350 XT and Tetric N - Ceram) evaluated in-vitro. Materials and Methods: This study was applied, analytical, experimental and longitudinal. 48 cylinders (16 cylinders per evaluated composite resin) of 6mm x 4mm, were made, which divided into two subgroups of 8 cylinders; and stored in physiological serum. These were submitted to the effect of Coca-Cola for 10 minutes per day and stored in physiological serum until the next immersion (24 hours); for 7 days. Data analysis was performed using Stata ® 12 Software. The ANOVA means test was applied.. Results: Displayed that the Filtek Z250 XT had a higher surface microhardness value, before (72.93 HV ±4.62) and after the erosive challenge (62.65 HV ±3.42); while Tetric N – Ceram was the resin wi...

El objetivo del presente estudio fue comparar el impacto de una bebida carbonatada sobre la microdureza superficial de tres resinas compuestas de nanorelleno (Filtek Z250 XT, Filtek Z350 XT y Tetric N - Ceram) evaluadas in-vitro. Este estudio fue de tipo aplicado, analítico y experimental, de corte longitudinal. Se elaboraron 48 cilindros (16 cilindros por resina compuesta evaluada) de 6mm x 4mm, los que fueron divididos en dos subgrupos de 8 cilindros; y almacenados en suero fisiológico. Estos fueron sometidos al efecto de Coca - Cola durante 10 minutos al día y almacenadas en suero fisiológico hasta la siguiente inmersión (24 horas); por 7 días. Los resultados mostraron que la resina Filtek Z250 XT tuvo mayor valor de microdureza superficial, antes (72,93 HV ±4,62) y después del desafío erosivo (62,65 HV ±3,42); mientras que Tetric N – Ceram fue la resina con menor valor de...