The structural, vibrational, morphological and magnetic properties of maghemite (γ-Fe2O3) nanoparticles functionalized with polar molecules EDTA(or H4Y) and H2Y are reported. The samples were functionalized before and after total synthesis of γ-Fe2O3 nanoparticles. The molecules are anchored on the monodentate mode on the nanoparticles surface. Transmission electron microscopy (TEM) revealed the formation of maghemite nanoparticles with small diameter of 4 nm for the sample functionalized upon synthesis and 7.6 and 6.9 nm for the samples functionalized with EDTA and H2Y after the formation of nanoparticles. Exchange bias phenomena were observed in some of the samples functionalized with EDTA at temperatures below 70 K. The presence of the bias effect was discussed in terms of the formation of a thin layer of a secondary phase like lepidocrocite, and the absence of this effect was expla...

Vacancy ordered maghemite (γ-Fe2O3) nanoparticles functionalized with nanohydroxyapatite (HAp – Ca10(PO4) 6(OH)2) have been successfully synthesized using an inexpensive co-precipitation chemical route. Evidence for the presence of vacancy order in maghemite was shown by the superstructure lines observed in X-ray diffraction. The adsorption of carboxyl groups of citric acid (C6H8O7) onto γ-Fe2O3 nanoparticles was investigated by FTIR, XPS and Mössbauer spectroscopy.

Vacancy ordered maghemite (γ-Fe2O3) nanoparticles functionalized with nanohydroxyapatite (HAp – Ca10(PO4) 6(OH)2) have been successfully synthesized using an inexpensive co-precipitation chemical route. Evidence for the presence of vacancy order in maghemite was shown by the superstructure lines observed in X-ray diffraction. The adsorption of carboxyl groups of citric acid (C6H8O7) onto γ-Fe2O3 nanoparticles was investigated by FTIR, XPS and Mössbauer spectroscopy. From XPS surface analysis, two binding energies related to oxygen were attributed to bindings between C6H8O7/γ- Fe2O3 and C6H8O7/HAp from an interfacial reaction promoted by strongly adsorbed H2O molecules at the surface of these nanomaterials.

Bare maghemite nanoparticles (Nps), binary, and ternary magnetic nanocomposites made with titanium dioxide (TiO2) and graphene oxide (GO) were synthesized by a facile and cheap coprecipitation chemical route, and used as magnetic nanoadsorbents to remove arsenite (As(III)) and arsenate (As(V)) from water. The structural, morphological, magnetic and surface properties were analyzed by XRD, TEM microscopy, FTIR and Raman vibrational spectroscopy, Mössbauer technique and N2 adsorption-desorption measurements. It was found that materials were composed of maghemite nanoparticles with crystallites diameters varying from 9 to 13 nm for bare Nps, binary and ternary nanocomposites, with these nanocomposites having a high percentage of maghemite phase (80%). The presence of TiO2 and GO in the binary and ternary materials was also confirmed. All the samples were found to show magnetic properties a...