In this study, magnetic nanocomposites were developed and used as adsorbents for lead and copper from aqueous media. Structural, surface, magnetic and textural properties of functionalized maghemite nanoparticles synthesized by alkaline co-precipitation were studied. The surfaces of the iron oxide nanoparticles (Nps) were modified with different chemical agents such as fatty and amino acids, silica (SiO2), mesoporous silica (SBA-15), hydroxyapatite, multiwall carbon nanotubes (MWCNTs) and ethylenediaminetetraacetic acid (EDTA), obtaining NPs with mean particle sizes ranging from 7 to 16 nm according to Rietveld refinement and TEM images analysis. The physicochemical surface properties of the functionalized materials were studied via zeta potential (z) and Fourier transform infrared (FTIR) spectroscopy. Mossbauer spectroscopy (MS) as a function of temperature and DC magnetometry were ¨ u...

Vacancy ordered maghemite (γ-Fe2O3) nanoparticles functionalized with nanohydroxyapatite (HAp – Ca10(PO4) 6(OH)2) have been successfully synthesized using an inexpensive co-precipitation chemical route. Evidence for the presence of vacancy order in maghemite was shown by the superstructure lines observed in X-ray diffraction. The adsorption of carboxyl groups of citric acid (C6H8O7) onto γ-Fe2O3 nanoparticles was investigated by FTIR, XPS and Mössbauer spectroscopy.

The structural, vibrational, morphological and magnetic properties of maghemite (γ-Fe2O3) nanoparticles functionalized with polar molecules EDTA(or H4Y) and H2Y are reported. The samples were functionalized before and after total synthesis of γ-Fe2O3 nanoparticles. The molecules are anchored on the monodentate mode on the nanoparticles surface. Transmission electron microscopy (TEM) revealed the formation of maghemite nanoparticles with small diameter of 4 nm for the sample functionalized upon synthesis and 7.6 and 6.9 nm for the samples functionalized with EDTA and H2Y after the formation of nanoparticles. Exchange bias phenomena were observed in some of the samples functionalized with EDTA at temperatures below 70 K. The presence of the bias effect was discussed in terms of the formation of a thin layer of a secondary phase like lepidocrocite, and the absence of this effect was expla...