Rough electrochromic phosphotungstic acid (PWA) films were fabricated by spraying a gel of phosphotungstate anions with a molar ratio of P:W = 1:12 onto glass substrates precoated with transparent and electrically conducting SnO2:F at 300 °C. The analysis by X-ray photoelectron spectroscopy (XPS) determined that the P:W molar ratio in the films was approximately 1:14. Infrared spectroscopy (IR) and X-ray diffraction (XRD) showed that the film is a polycrystalline phosphotungstic acid. SEM micrographs showed that the films present a rough morphology based on fiber-shape bridges. Optoelectrochemical measurements demonstrated pronounced electrochromism in the PWA films upon H+ intercalation/deintercalation with a high diffuse reflectance (Rd) and transmittance (Td). We found for as-deposited films that Rd/total reflectance (Rt) and Td/total transmittance (Tt) at 550 nm was around 0.83 and ...

OBJETIVO: Es importante conocer las propiedades mecánicas de los materiales dentales para poder determinar críticamente su comportamiento y no limitarnos únicamente a la evaluación clínica. Por esa razón, el objetivo de este estudio fue comparar la microdureza de cuatro cementos resinosos de uso odontológico teniendo en cuenta que existe correlación entre esta propiedad mecánica y el comportamiento clínico del material.MATERIALES Y MÉTODOS: Se confeccionaron seis cuerpos de prueba para cada cemento evaluado: RelyXTM ARC(3M ESPE) = G1, Multilink® (IVOCLAR VIVADENT) = G2, MaxCem EliteTM (KERR CORPORATION) = G3 y RelyXTMU200 (3M ESPE) = G4, los que fueron almacenados durante 48 horas a temperatura ambiente y sometidos al ensayo deMicrodureza Vickers (VMH) con 200 g-f durante 10 segundos.RESULTADOS: Para el cemento resinoso dual convencional (grupo control) G1 el valor promedi...