Residual commercial polystyrene samples (PScr) have been undergone to thermal decomposition processes between 433 hand 673 K (160 at 400 °C). The analyses of the distilled have confirmed that PS has been transformed into styrene with a yield from 45 to 60%. The monomer obtained has been polymerized in suspension using benzoyl peroxide like initiator and divinylbenzene (DVB) in proportions of 2, 6 and 10%. The obtained microspheres of copolymer (PS-DVB) have been sulfonated. After characterization, the results showed that 6% of DVB, presents similar characteristic than the commercial strongly acid cationic exchange resin Sybron Chemicals Inc. Ionac ® C-249.

Muestras de poliestireno comercial residual (PScr) se han sometido a procesos de descomposición térmica entre 433 a 673 K (160 a 400 °C). Los análisis del destilado han confirmado que el PS ha sido transformado a estireno con un rendimiento entre el 45 al 60%. El monómero obtenido se ha polimerizado en suspensión usando peróxido de benzoilo como iniciador y divinilbenceno (DVB) en proporciones de 2, 6 y 10%. Las microesferas obtenidas del copolímero (PS-DVB) han sido sulfonadas. El resultado, después de la caracterización, fue aquel del 6% de DVB presenta características similares a las de la resina comercial de intercambio catiónico fuertemente ácida Sybron Chemicals Inc. Ionac ® C-249.