A hydrogel with β-chitosan matrix that retards the release of platelet-derived growth factor - BB (PDGF - BB), which is part of the platelet lysate (LP) obtained from platelet rich plasma (PRP), was developed. The hydrogel was composed of a solution of 1.5 % (w/v) β-chitosan in 2 % (v/v) acetic acid, 6% or 12 % LP (v/v) and glutaraldehyde 0.03M. The β-chitosan used as raw material had 12.47 % of average relative humidity, 94.53 of average deacetylation degree and an estimated average molecular weight of 145.94 kDa; important attributes to formulate a hydrogel of semi-solid consistency, colorless and easy to handle. Delayed release was achieved with the 12 % LP hydrogel since the release of PDGF – BB does not differ significantly (p <0.05) by varying the pH from 6.5 (5 491.42 pg of PDGF – BB/mL of LP) to 7.4 (5 387.39 pg of PDGF – BB/mL of LP) after 32 hours. In contrast, the ...

Se diseñó un hidrogel que tiene como matriz al β-quitosano y que retarda la liberación del factor de crecimiento derivado de plaquetas-BB (PDGF-BB). PDGF-BB forma parte del lisado plaquetario (LP), el cual se obtuvo a partir del plasma rico en plaquetas (PRP) después de someterlo a un shock térmico. El β-quitosano fue caracterizado en porcentaje de humedad, grado de desacetilación y peso molecular promedio, usando técnicas como gravimetría, titulación potenciométrica y medición de viscosidad con el viscosímetro de Ostwald, respectivamente. Se tuvo en cuenta que el intersticio de una úlcera cutánea pasa por variaciones en el pH; motivo por el cual este trabajo busca estudiar la influencia del pH del medio en la liberación de PDGF-BB de la matriz de β-quitosano. Se obtuvieron los siguientes resultados: el β-quitosano con el que se trabajó, tiene 12.47% de humedad, un gr...