In the present work there describes a series of synthesis of materials type NaMF3 using salts of Co, Ni and Mn as precursors, for use as positive electrodes in lithium battery, which uses lithium as the negative electrode. The synthesis product obtained was characterized with structurally DRX, the particle size distribution was observed by scanning electron microscope. For the electrochemical study was assembled a stack type CR2032 which was carried out studies of cyclical behavior of loading and unloading to check if it behaves like a secondary battery. The results obtained show be this synthesis method proposed is a quick and easy method for obtaining this type of cathodes

En el presente trabajo se describe una serie de síntesis de materiales tipo NaMF3 utilizando sales de Co, Ni y Mn como precursores, para ser utilizados como electrodos positivos en una pila de litio, donde se utiliza litio como electrodo negativo. El producto obtenido de síntesis se caracterizo estructuralmente con DRX, la distribución del tamaño de partícula fueron observadas mediante Microscopio Electrónico de Barrido. Para el estudio electroquímico se ensamblo una pila tipo CR2032 a la cual se realizo estudios de comportamiento cíclico de carga y descarga para comprobar si se comporta como una pila secundaria. Los resultados obtenidos muestran ser este método de síntesis propuesto un método rápido y sencillo para la obtención de este tipo de cátodos.