This paper describes the synthesis and characterization of copper nanoparticles (O) - Cu NPs (O) - applying the method assisted polyol ( glycolysis ) microwave ( MW ) , using an organic synthetic precursor of Cu ( II ) previously synthesized and polyethylene terephthalate ( PET ), the depolymerization reaction by MW was conducted with ethylene glycol (EG) by its high dielectric constant ( 41.4 at 298K ) and dielectric loss , allowing it to be rapidly heated with microwave radiation and achieving speed reduction rate metal ions in the system. At this stage , the formed byproducts are terephthalate , bis ( 2-hydroxyethyl ) ( BHET ) , dimers of BHET and / or oligomers thereof, which serve as stabilizing agents and to achieve encapsulate NPsCu (O) , preventing their autoxidation . Subsequently, the system was subjected to an ultrasonic pulse ( U.S. ) , which due to the internal cavilación g...

El presente estudio describe la síntesis y caracterización de las nanopartículas de cobre(O) - NPs Cu(O) - aplicando el método poliol(glicólisis) asistida por microondas (MW), utilizando un precursor sintético orgánico de Cu(II) previamente sintetizado y Tereftalato de polietileno (PET); la reacción de despolimerización por MW fue realizado con etilenglicol (EG) por su alta constante dieléctrica ( 41,4 a 298K) y pérdida dieléctrica, permitiendo ser calentado rápidamente con radiación microondas y logrando acelerar la velocidad de reducción de los iones metálicos del sistema. En esta etapa, los productos secundarios formados son tereftalato de bis-(2-hidroxietilo) (BHET), dímeros del BHET y/o sus oligómeros, que sirven como agentes estabilizantes y logran encapsular a las NPsCu(O), evitando su autoxidación. Posteriormente, el sistema fue sometido a un pulso ultrasónico...