Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termociclado

Descripción del Articulo

Objetivo: El propósito del estudio fue comparar la resistencia al cizallamiento y el índice adhesivo remanente (ARI) utilizando dos tipos de cementos, TransbondTM XT (3M Unitek, Monrovia, California, USA) y OrthoCem (FGM, Joinville, Brazil). Materiales y Métodos: Sesenta dientes incisivos de bovino...

Descripción completa

Detalles Bibliográficos
Autor: Ramírez Mejía, María Jimena
Formato: tesis de grado
Fecha de Publicación:2017
Institución:Universidad Peruana de Ciencias Aplicadas
Repositorio:UPC-Institucional
Lenguaje:español
OAI Identifier:oai:repositorioacademico.upc.edu.pe:10757/621715
Enlace del recurso:http://hdl.handle.net/10757/621715
Nivel de acceso:acceso abierto
Materia:Ortodoncia
Esmalte dental
Materiales dentales
Agentes de control de microorganismos
Estudios de casos y controles
Odontología
https://purl.org/pe-repo/ocde/ford#3.02.14
id UUPC_d2fbba799390a902e55dcd3af3251497
oai_identifier_str oai:repositorioacademico.upc.edu.pe:10757/621715
network_acronym_str UUPC
network_name_str UPC-Institucional
repository_id_str 2670
dc.title.es.fl_str_mv Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termociclado
title Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termociclado
spellingShingle Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termociclado
Ramírez Mejía, María Jimena
Ortodoncia
Esmalte dental
Materiales dentales
Agentes de control de microorganismos
Estudios de casos y controles
Odontología
https://purl.org/pe-repo/ocde/ford#3.02.14
title_short Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termociclado
title_full Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termociclado
title_fullStr Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termociclado
title_full_unstemmed Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termociclado
title_sort Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termociclado
author Ramírez Mejía, María Jimena
author_facet Ramírez Mejía, María Jimena
author_role author
dc.contributor.advisor.fl_str_mv Córdova Berrocal, Andrés
dc.contributor.author.fl_str_mv Ramírez Mejía, María Jimena
dc.subject.es.fl_str_mv Ortodoncia
Esmalte dental
Materiales dentales
Agentes de control de microorganismos
Estudios de casos y controles
Odontología
topic Ortodoncia
Esmalte dental
Materiales dentales
Agentes de control de microorganismos
Estudios de casos y controles
Odontología
https://purl.org/pe-repo/ocde/ford#3.02.14
dc.subject.ocde.es_PE.fl_str_mv https://purl.org/pe-repo/ocde/ford#3.02.14
description Objetivo: El propósito del estudio fue comparar la resistencia al cizallamiento y el índice adhesivo remanente (ARI) utilizando dos tipos de cementos, TransbondTM XT (3M Unitek, Monrovia, California, USA) y OrthoCem (FGM, Joinville, Brazil). Materiales y Métodos: Sesenta dientes incisivos de bovino recién extraídos fueron divididos al azar en 4 grupos (n=15). En los Grupos A y B, los brackets fueron cementados con TransbondTM XT y OrthoCem respectivamente. En el Grupo C, se utilizó TransbondTM XT con 500 ciclos de termociclado y en el Grupo D se utilizó OrthoCem con 500 ciclos de termociclado. Se midió la resistencia al cizallamiento con la máquina de ensayo universal Instron® (3382, Instron Corp., Canton, Mass) a una velocidad de 0.5mm/min y se registraron los datos en megapascales (MPa). Después de la prueba de cizallamiento, fue registrado el índice ARI con el Microscopio Digital Dino-Lite AM4515T8 Edge a 40x. Resultados: El cemento TransbondTM XT sin termociclado obtuvo una media de 22.68 MPa, a diferencia del cemento OrthoCem el cual obtuvo 12.58 MPa de resistencia al cizallamiento. Después del termociclado, el cemento TransbondTM XT obtuvo 14.79 MPa a diferencia del OrthoCem, el cual consiguió 7.97 MPa. Conclusión: TransbondTM XT obtuvo valores más elevados de resistencia de unión al esmalte con y sin termociclado en comparación al OrthoCem
publishDate 2017
dc.date.accessioned.none.fl_str_mv 2017-06-27T00:31:20Z
dc.date.available.none.fl_str_mv 2017-06-27T00:31:20Z
dc.date.issued.fl_str_mv 2017-06-05
dc.type.es.fl_str_mv info:eu-repo/semantics/bachelorThesis
dc.type.other.es_PE.fl_str_mv Tesis
dc.type.coar.es_PE.fl_str_mv http://purl.org/coar/resource_type/c_7a1f
format bachelorThesis
dc.identifier.citation.es_PE.fl_str_mv 1. Ramírez Mejía MJ. Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termociclado. Universidad Peruana de Ciencias Aplicadas (UPC); 2017.
dc.identifier.doi.es_PE.fl_str_mv 10.19083/tesis/621715
dc.identifier.uri.none.fl_str_mv http://hdl.handle.net/10757/621715
identifier_str_mv 1. Ramírez Mejía MJ. Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termociclado. Universidad Peruana de Ciencias Aplicadas (UPC); 2017.
10.19083/tesis/621715
url http://hdl.handle.net/10757/621715
dc.language.iso.es_PE.fl_str_mv spa
language spa
dc.relation.ispartof.fl_str_mv SUNEDU
dc.rights.es_PE.fl_str_mv info:eu-repo/semantics/openAccess
dc.rights.uri.*.fl_str_mv http://creativecommons.org/licenses/by-nc-nd/4.0/
dc.rights.coar.es_PE.fl_str_mv http://purl.org/coar/access_right/c_abf2
eu_rights_str_mv openAccess
rights_invalid_str_mv http://creativecommons.org/licenses/by-nc-nd/4.0/
http://purl.org/coar/access_right/c_abf2
dc.format.es.fl_str_mv application/pdf
application/epub
application/msword
dc.publisher.es.fl_str_mv Universidad Peruana de Ciencias Aplicadas (UPC)
dc.publisher.country.es_PE.fl_str_mv PE
dc.source.es_PE.fl_str_mv Universidad Peruana de Ciencias Aplicadas (UPC)
Repositorio Académico - UPC
dc.source.none.fl_str_mv reponame:UPC-Institucional
instname:Universidad Peruana de Ciencias Aplicadas
instacron:UPC
instname_str Universidad Peruana de Ciencias Aplicadas
instacron_str UPC
institution UPC
reponame_str UPC-Institucional
collection UPC-Institucional
bitstream.url.fl_str_mv https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/1/license.txt
https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/2/RAMIREZ_MM.pdf
https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/3/RAMIREZ_MM.epub
https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/4/RAMIREZ_MM.docx
https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/5/RAMIREZ_MMficha.pdf
https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/6/RAMIREZ_MM.pdf.txt
https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/8/RAMIREZ_MM.docx.txt
https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/9/RAMIREZ_MMficha.pdf.txt
https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/14/RAMIREZ_MM.pdf.jpg
https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/15/RAMIREZ_MMficha.pdf.jpg
https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/11/license_url
https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/12/license_text
https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/13/license_rdf
bitstream.checksum.fl_str_mv 255616c2e22876c8a237cd50f1bc22a3
d1565c31de837deafca8fba19fd21184
96c6fd414063b34b08ead3add42dfc0c
64b1eb808fa4b948f8924caed533a31d
6b2c244e663aafe9a5a0bde470dd0e2a
f18ffccc3d602ac4ac6682dd3f9baab8
fc9d63b1bd4a1b54fe531b3f65d295d2
0b0d40bea8482df673b8c25851e8b0d3
57ce6f19b90ebd59796886d2b74f603e
de494b41209eca878b3232a957dff58a
4afdbb8c545fd630ea7db775da747b2f
d41d8cd98f00b204e9800998ecf8427e
d41d8cd98f00b204e9800998ecf8427e
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
MD5
MD5
MD5
MD5
MD5
MD5
MD5
MD5
MD5
MD5
MD5
repository.name.fl_str_mv Repositorio académico upc
repository.mail.fl_str_mv upc@openrepository.com
_version_ 1846065332059373568
spelling b9965390581495b7793f55fc6cff39ebCórdova Berrocal, Andrésc909ffb437302a0c05f8f4028e7580bc500Ramírez Mejía, María Jimena2017-06-27T00:31:20Z2017-06-27T00:31:20Z2017-06-051. Ramírez Mejía MJ. Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termociclado. Universidad Peruana de Ciencias Aplicadas (UPC); 2017.10.19083/tesis/621715http://hdl.handle.net/10757/621715Objetivo: El propósito del estudio fue comparar la resistencia al cizallamiento y el índice adhesivo remanente (ARI) utilizando dos tipos de cementos, TransbondTM XT (3M Unitek, Monrovia, California, USA) y OrthoCem (FGM, Joinville, Brazil). Materiales y Métodos: Sesenta dientes incisivos de bovino recién extraídos fueron divididos al azar en 4 grupos (n=15). En los Grupos A y B, los brackets fueron cementados con TransbondTM XT y OrthoCem respectivamente. En el Grupo C, se utilizó TransbondTM XT con 500 ciclos de termociclado y en el Grupo D se utilizó OrthoCem con 500 ciclos de termociclado. Se midió la resistencia al cizallamiento con la máquina de ensayo universal Instron® (3382, Instron Corp., Canton, Mass) a una velocidad de 0.5mm/min y se registraron los datos en megapascales (MPa). Después de la prueba de cizallamiento, fue registrado el índice ARI con el Microscopio Digital Dino-Lite AM4515T8 Edge a 40x. Resultados: El cemento TransbondTM XT sin termociclado obtuvo una media de 22.68 MPa, a diferencia del cemento OrthoCem el cual obtuvo 12.58 MPa de resistencia al cizallamiento. Después del termociclado, el cemento TransbondTM XT obtuvo 14.79 MPa a diferencia del OrthoCem, el cual consiguió 7.97 MPa. Conclusión: TransbondTM XT obtuvo valores más elevados de resistencia de unión al esmalte con y sin termociclado en comparación al OrthoCemObjective: The aim of this study was to compare the shear bond strength (SBS) and adhesive remnant index (ARI) of two dental cements, TransbondTM XT (3M Unitek, Monrovia, California, USA) and OrthoCem (FGM, Joinville, Brazil). Materials and Methods: Sixty freshly extracted bovine incisors were randomly divided into four groups (n=15). In Groups A and B brackets were bonded with TransbondTM XT and OrthoCem respectively. In Group C brackets were bonded with TransbondTM XT with 500 thermocycles and in Group D brackets were bonded with OrthoCem with 500 thermocycles. The SBSs were measured with an Instron Universal testing machine (3382, Instron Corp., Canton, Mass) at a crosshead speed of 0.5 mn/min, data were recorded in megapascals (MPa). After the failure, the ARI was observed in a Digital Microscope Dino-Lite AM4515T8 Edge at 40x. Results: TransbondTM XT without thermocycling obtained a mean of 22.68 MPa and OrthoCem an average of 12.58 MPa of SBS. After thermocycling, TransbondTM XT obtained 14.79MPa and OrthoCem obtained a mean of 7.97 MPa. Conclusion: TransbondTM XT has higher values of SBS with or without thermocycling than OrthoCem.Tesisapplication/pdfapplication/epubapplication/mswordspaUniversidad Peruana de Ciencias Aplicadas (UPC)PEinfo:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by-nc-nd/4.0/http://purl.org/coar/access_right/c_abf2Universidad Peruana de Ciencias Aplicadas (UPC)Repositorio Académico - UPCreponame:UPC-Institucionalinstname:Universidad Peruana de Ciencias Aplicadasinstacron:UPCOrtodonciaEsmalte dentalMateriales dentalesAgentes de control de microorganismosEstudios de casos y controlesOdontologíahttps://purl.org/pe-repo/ocde/ford#3.02.14Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termocicladoinfo:eu-repo/semantics/bachelorThesisTesishttp://purl.org/coar/resource_type/c_7a1fSUNEDUUniversidad Peruana de Ciencias Aplicadas (UPC). Facultad de Ciencias de la SaludLicenciaturaOdontologíaCirujano Dentista2018-06-18T13:07:35ZObjetivo: El propósito del estudio fue comparar la resistencia al cizallamiento y el índice adhesivo remanente (ARI) utilizando dos tipos de cementos, TransbondTM XT (3M Unitek, Monrovia, California, USA) y OrthoCem (FGM, Joinville, Brazil). Materiales y Métodos: Sesenta dientes incisivos de bovino recién extraídos fueron divididos al azar en 4 grupos (n=15). En los Grupos A y B, los brackets fueron cementados con TransbondTM XT y OrthoCem respectivamente. En el Grupo C, se utilizó TransbondTM XT con 500 ciclos de termociclado y en el Grupo D se utilizó OrthoCem con 500 ciclos de termociclado. Se midió la resistencia al cizallamiento con la máquina de ensayo universal Instron® (3382, Instron Corp., Canton, Mass) a una velocidad de 0.5mm/min y se registraron los datos en megapascales (MPa). Después de la prueba de cizallamiento, fue registrado el índice ARI con el Microscopio Digital Dino-Lite AM4515T8 Edge a 40x. Resultados: El cemento TransbondTM XT sin termociclado obtuvo una media de 22.68 MPa, a diferencia del cemento OrthoCem el cual obtuvo 12.58 MPa de resistencia al cizallamiento. Después del termociclado, el cemento TransbondTM XT obtuvo 14.79 MPa a diferencia del OrthoCem, el cual consiguió 7.97 MPa. Conclusión: TransbondTM XT obtuvo valores más elevados de resistencia de unión al esmalte con y sin termociclado en comparación al OrthoCemObjective: The aim of this study was to compare the shear bond strength (SBS) and adhesive remnant index (ARI) of two dental cements, TransbondTM XT (3M Unitek, Monrovia, California, USA) and OrthoCem (FGM, Joinville, Brazil). Materials and Methods: Sixty freshly extracted bovine incisors were randomly divided into four groups (n=15). In Groups A and B brackets were bonded with TransbondTM XT and OrthoCem respectively. In Group C brackets were bonded with TransbondTM XT with 500 thermocycles and in Group D brackets were bonded with OrthoCem with 500 thermocycles. The SBSs were measured with an Instron Universal testing machine (3382, Instron Corp., Canton, Mass) at a crosshead speed of 0.5 mn/min, data were recorded in megapascals (MPa). After the failure, the ARI was observed in a Digital Microscope Dino-Lite AM4515T8 Edge at 40x. Results: TransbondTM XT without thermocycling obtained a mean of 22.68 MPa and OrthoCem an average of 12.58 MPa of SBS. After thermocycling, TransbondTM XT obtained 14.79MPa and OrthoCem obtained a mean of 7.97 MPa. Conclusion: TransbondTM XT has higher values of SBS with or without thermocycling than OrthoCem.https://purl.org/pe-repo/renati/type#tesishttps://purl.org/pe-repo/renati/nivel#tituloProfesionalLICENSElicense.txtlicense.txttext/plain; charset=utf-81702https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/1/license.txt255616c2e22876c8a237cd50f1bc22a3MD51falseORIGINALRAMIREZ_MM.pdfRAMIREZ_MM.pdfapplication/pdf1153939https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/2/RAMIREZ_MM.pdfd1565c31de837deafca8fba19fd21184MD52trueRAMIREZ_MM.epubRAMIREZ_MM.epubapplication/epub875024https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/3/RAMIREZ_MM.epub96c6fd414063b34b08ead3add42dfc0cMD53false2087-06-05RAMIREZ_MM.docxRAMIREZ_MM.docxapplication/vnd.openxmlformats-officedocument.wordprocessingml.document2584638https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/4/RAMIREZ_MM.docx64b1eb808fa4b948f8924caed533a31dMD54false2087-06-05RAMIREZ_MMficha.pdfRAMIREZ_MMficha.pdfapplication/pdf76585https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/5/RAMIREZ_MMficha.pdf6b2c244e663aafe9a5a0bde470dd0e2aMD55falseTEXTRAMIREZ_MM.pdf.txtRAMIREZ_MM.pdf.txtExtracted Texttext/plain31495https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/6/RAMIREZ_MM.pdf.txtf18ffccc3d602ac4ac6682dd3f9baab8MD56false2087-06-05RAMIREZ_MM.docx.txtRAMIREZ_MM.docx.txtExtracted texttext/plain31506https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/8/RAMIREZ_MM.docx.txtfc9d63b1bd4a1b54fe531b3f65d295d2MD58false2087-06-05RAMIREZ_MMficha.pdf.txtRAMIREZ_MMficha.pdf.txtExtracted Texttext/plain2https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/9/RAMIREZ_MMficha.pdf.txt0b0d40bea8482df673b8c25851e8b0d3MD59falseTHUMBNAILRAMIREZ_MM.pdf.jpgRAMIREZ_MM.pdf.jpgGenerated Thumbnailimage/jpeg27849https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/14/RAMIREZ_MM.pdf.jpg57ce6f19b90ebd59796886d2b74f603eMD514false2087-06-05RAMIREZ_MMficha.pdf.jpgRAMIREZ_MMficha.pdf.jpgGenerated Thumbnailimage/jpeg68805https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/15/RAMIREZ_MMficha.pdf.jpgde494b41209eca878b3232a957dff58aMD515falseCC-LICENSElicense_urllicense_urltext/plain; charset=utf-849https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/11/license_url4afdbb8c545fd630ea7db775da747b2fMD511falselicense_textlicense_texttext/html; charset=utf-80https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/12/license_textd41d8cd98f00b204e9800998ecf8427eMD512falselicense_rdflicense_rdfapplication/rdf+xml; charset=utf-80https://repositorioacademico.upc.edu.pe/bitstream/10757/621715/13/license_rdfd41d8cd98f00b204e9800998ecf8427eMD513falseCONVERTED2_356410210757/621715oai:repositorioacademico.upc.edu.pe:10757/6217152025-07-19 20:28:27.064Repositorio académico upcupc@openrepository.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
score 13.134565
Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termociclado
Nota importante:
La información contenida en este registro es de entera responsabilidad de la institución que gestiona el repositorio institucional donde esta contenido este documento o set de datos. El CONCYTEC no se hace responsable por los contenidos (publicaciones y/o datos) accesibles a través del Repositorio Nacional Digital de Ciencia, Tecnología e Innovación de Acceso Abierto (ALICIA).

Ejemplares Similares