Resistencia a la compresión de carillas cerámicas de disilicato de litio cementadas con cemento resinoso dual y cemento resinoso dual autoadhesivo en premolares maxilares
Descripción del Articulo
ABSTRACT: The aim of this work was to establish the resistance degree to the compression force in porcelain laminate. In this experimental in vitro study 30 premolars were selected and randomly divided in groups of 15 teeth each, subsequently specimens were prepared for ceramic veneers 0.5 mm thick....
| Autores: | , , |
|---|---|
| Formato: | artículo |
| Fecha de Publicación: | 2015 |
| Institución: | Universidad de San Martín de Porres |
| Repositorio: | USMP-Institucional |
| Lenguaje: | español |
| OAI Identifier: | oai:repositorio.usmp.edu.pe:20.500.12727/6206 |
| Enlace del recurso: | https://hdl.handle.net/20.500.12727/6206 https://doi.org/10.4067/S0718-381X2015000100013 |
| Nivel de acceso: | acceso abierto |
| Materia: | Coronas con frente estético Cementos de resina Fracturas por compresión Cementación https://purl.org/pe-repo/ocde/ford#3.02.00 |
| id |
USMP_304d3c6c4783c9560268bb58954d16bc |
|---|---|
| oai_identifier_str |
oai:repositorio.usmp.edu.pe:20.500.12727/6206 |
| network_acronym_str |
USMP |
| network_name_str |
USMP-Institucional |
| repository_id_str |
2089 |
| dc.title.es_PE.fl_str_mv |
Resistencia a la compresión de carillas cerámicas de disilicato de litio cementadas con cemento resinoso dual y cemento resinoso dual autoadhesivo en premolares maxilares |
| dc.title.alternative.es_PE.fl_str_mv |
Compressive resistance of lithium disilicate porcelain laminate veneers cemented with dual resin cement and self-adhesive dual resin cement in upper premolars |
| title |
Resistencia a la compresión de carillas cerámicas de disilicato de litio cementadas con cemento resinoso dual y cemento resinoso dual autoadhesivo en premolares maxilares |
| spellingShingle |
Resistencia a la compresión de carillas cerámicas de disilicato de litio cementadas con cemento resinoso dual y cemento resinoso dual autoadhesivo en premolares maxilares Mellado Alfaro, Brando Coronas con frente estético Cementos de resina Fracturas por compresión Cementación https://purl.org/pe-repo/ocde/ford#3.02.00 |
| title_short |
Resistencia a la compresión de carillas cerámicas de disilicato de litio cementadas con cemento resinoso dual y cemento resinoso dual autoadhesivo en premolares maxilares |
| title_full |
Resistencia a la compresión de carillas cerámicas de disilicato de litio cementadas con cemento resinoso dual y cemento resinoso dual autoadhesivo en premolares maxilares |
| title_fullStr |
Resistencia a la compresión de carillas cerámicas de disilicato de litio cementadas con cemento resinoso dual y cemento resinoso dual autoadhesivo en premolares maxilares |
| title_full_unstemmed |
Resistencia a la compresión de carillas cerámicas de disilicato de litio cementadas con cemento resinoso dual y cemento resinoso dual autoadhesivo en premolares maxilares |
| title_sort |
Resistencia a la compresión de carillas cerámicas de disilicato de litio cementadas con cemento resinoso dual y cemento resinoso dual autoadhesivo en premolares maxilares |
| author |
Mellado Alfaro, Brando |
| author_facet |
Mellado Alfaro, Brando Anchelia Ramirez, Shilla Quea Cahuana, Eduardo |
| author_role |
author |
| author2 |
Anchelia Ramirez, Shilla Quea Cahuana, Eduardo |
| author2_role |
author author |
| dc.contributor.author.fl_str_mv |
Mellado Alfaro, Brando Anchelia Ramirez, Shilla Quea Cahuana, Eduardo |
| dc.subject.es_PE.fl_str_mv |
Coronas con frente estético Cementos de resina Fracturas por compresión Cementación |
| topic |
Coronas con frente estético Cementos de resina Fracturas por compresión Cementación https://purl.org/pe-repo/ocde/ford#3.02.00 |
| dc.subject.ocde.es_PE.fl_str_mv |
https://purl.org/pe-repo/ocde/ford#3.02.00 |
| description |
ABSTRACT: The aim of this work was to establish the resistance degree to the compression force in porcelain laminate. In this experimental in vitro study 30 premolars were selected and randomly divided in groups of 15 teeth each, subsequently specimens were prepared for ceramic veneers 0.5 mm thick. The first group was cemented with dual resin cement (CRD) and the second with dual adhesive resin cement (CRDA). After cementation was tested in a universal test machine until fracture compression forces occurred (N) at 1 mm / min speed. Student´s t-test (a= 0.05) was used to compare means. The results showed statistically significant differences (p<0.05) between groups. The mean compressive strength for cemented samples was 677.47 N and 550.0 N for dual resin cement and auto-adhesive dual resin cement respectively. It was found that porcelain laminate veneers made of lithium disilicate and cemented with CRD have greater resistance to compression force compered to CRDA. |
| publishDate |
2015 |
| dc.date.accessioned.none.fl_str_mv |
2020-06-12T21:31:14Z |
| dc.date.available.none.fl_str_mv |
2020-06-12T21:31:14Z |
| dc.date.issued.fl_str_mv |
2015-04 |
| dc.type.es_PE.fl_str_mv |
info:eu-repo/semantics/article |
| format |
article |
| dc.identifier.citation.es_PE.fl_str_mv |
Mellado B., Anchelia S., Quea E. Compressive resistance of lithium disilicate porcelain laminate veneers cemented with dual resin cement and self-adhesive dual resin cement in upper premolars. Int. J. Odontostomat. 2015; 9(1): 85-89. |
| dc.identifier.uri.none.fl_str_mv |
https://hdl.handle.net/20.500.12727/6206 |
| dc.identifier.doi.none.fl_str_mv |
https://doi.org/10.4067/S0718-381X2015000100013 |
| identifier_str_mv |
Mellado B., Anchelia S., Quea E. Compressive resistance of lithium disilicate porcelain laminate veneers cemented with dual resin cement and self-adhesive dual resin cement in upper premolars. Int. J. Odontostomat. 2015; 9(1): 85-89. |
| url |
https://hdl.handle.net/20.500.12727/6206 https://doi.org/10.4067/S0718-381X2015000100013 |
| dc.language.iso.es_PE.fl_str_mv |
spa |
| language |
spa |
| dc.relation.ispartof.none.fl_str_mv |
urn:issn:0034-9887 |
| dc.relation.ispartofseries.none.fl_str_mv |
International journal of odontostomatology;vol. 9, no. 1 |
| dc.rights.es_PE.fl_str_mv |
info:eu-repo/semantics/openAccess |
| dc.rights.uri.es_PE.fl_str_mv |
https://creativecommons.org/licenses/by-nc/4.0/ |
| eu_rights_str_mv |
openAccess |
| rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc/4.0/ |
| dc.format.extent.es_PE.fl_str_mv |
pp. 85-89 |
| dc.publisher.es_PE.fl_str_mv |
Universidad de La Frontera. Facultad de Medicina |
| dc.publisher.country.es_PE.fl_str_mv |
CL |
| dc.source.es_PE.fl_str_mv |
Repositorio Académico USMP Universidad de San Martín de Porres - USMP |
| dc.source.none.fl_str_mv |
reponame:USMP-Institucional instname:Universidad de San Martín de Porres instacron:USMP |
| instname_str |
Universidad de San Martín de Porres |
| instacron_str |
USMP |
| institution |
USMP |
| reponame_str |
USMP-Institucional |
| collection |
USMP-Institucional |
| bitstream.url.fl_str_mv |
https://repositorio.usmp.edu.pe/bitstream/20.500.12727/6206/1/anchelia_rsfmh-2015.pdf https://repositorio.usmp.edu.pe/bitstream/20.500.12727/6206/2/license.txt https://repositorio.usmp.edu.pe/bitstream/20.500.12727/6206/3/anchelia_rsfmh-2015.pdf.txt https://repositorio.usmp.edu.pe/bitstream/20.500.12727/6206/4/anchelia_rsfmh-2015.pdf.jpg |
| bitstream.checksum.fl_str_mv |
dcbc894c4e780a5720bd73f83e521837 8a4605be74aa9ea9d79846c1fba20a33 c4b8fa5faca989e188d9f4a200f00858 22edff3f4a39eabf5d49ea2b486d0558 |
| bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
| repository.name.fl_str_mv |
REPOSITORIO ACADEMICO USMP |
| repository.mail.fl_str_mv |
repositorio@usmp.pe |
| _version_ |
1846890192505405440 |
| spelling |
Mellado Alfaro, BrandoAnchelia Ramirez, ShillaQuea Cahuana, Eduardo2020-06-12T21:31:14Z2020-06-12T21:31:14Z2015-04Mellado B., Anchelia S., Quea E. Compressive resistance of lithium disilicate porcelain laminate veneers cemented with dual resin cement and self-adhesive dual resin cement in upper premolars. Int. J. Odontostomat. 2015; 9(1): 85-89.https://hdl.handle.net/20.500.12727/6206https://doi.org/10.4067/S0718-381X2015000100013ABSTRACT: The aim of this work was to establish the resistance degree to the compression force in porcelain laminate. In this experimental in vitro study 30 premolars were selected and randomly divided in groups of 15 teeth each, subsequently specimens were prepared for ceramic veneers 0.5 mm thick. The first group was cemented with dual resin cement (CRD) and the second with dual adhesive resin cement (CRDA). After cementation was tested in a universal test machine until fracture compression forces occurred (N) at 1 mm / min speed. Student´s t-test (a= 0.05) was used to compare means. The results showed statistically significant differences (p<0.05) between groups. The mean compressive strength for cemented samples was 677.47 N and 550.0 N for dual resin cement and auto-adhesive dual resin cement respectively. It was found that porcelain laminate veneers made of lithium disilicate and cemented with CRD have greater resistance to compression force compered to CRDA.El objetivo de este trabajo fue determinar el grado de resistencia a la fuerza de compresión de las carillas de cerámica de disilicato de litio cementadas con dos agentes de resina dual en premolares maxilares. En este estudio experimental in vitro se seleccionaron 30 premolares maxilares, los cuales fueron divididos aleatoriamente en dos grupos de 15 dientes cada uno; posteriormente los especímenes fueron preparados para recibir carillas de cerámica de 0,5 mm de grosor. Las carillas de grupo 1 se cementaron con un cemento resinoso dual (CRD) y las del grupo 2 con un cemento de resina dual autoadhesivo (CRDA). Luego de cementadas fueron puestas a prueba en una máquina de ensayo universal hasta su fractura por fuerzas de compresión (N) a una velocidad de 1 mm/min. Para la comparación de medias se utilizó la prueba t de Student (a= 0,05). Los resultados mostraron diferencias estadísticamente significativas (p<0,05) entre los grupos estudiados. La media de la resistencia a la compresión de las muestras cementadas con cemento resinoso dual y cemento resinoso dual autoadhesivo fue de 677,47 N y 5500 N, respectivamente. Se determinó que las carillas de cerámica de disilicato de litio cementadas con CRD tienen mayor resistencia a la fuerza de compresión respecto a las cementadas con CRDA.pp. 85-89spaUniversidad de La Frontera. Facultad de MedicinaCLurn:issn:0034-9887International journal of odontostomatology;vol. 9, no. 1info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc/4.0/Repositorio Académico USMPUniversidad de San Martín de Porres - USMPreponame:USMP-Institucionalinstname:Universidad de San Martín de Porresinstacron:USMPCoronas con frente estéticoCementos de resinaFracturas por compresiónCementaciónhttps://purl.org/pe-repo/ocde/ford#3.02.00Resistencia a la compresión de carillas cerámicas de disilicato de litio cementadas con cemento resinoso dual y cemento resinoso dual autoadhesivo en premolares maxilaresCompressive resistance of lithium disilicate porcelain laminate veneers cemented with dual resin cement and self-adhesive dual resin cement in upper premolarsinfo:eu-repo/semantics/articleMedicina HumanaUniversidad de San Martín de Porres. Facultad de Medicina HumanaMedicinaORIGINALanchelia_rsfmh-2015.pdfanchelia_rsfmh-2015.pdfTrabajoapplication/pdf208932https://repositorio.usmp.edu.pe/bitstream/20.500.12727/6206/1/anchelia_rsfmh-2015.pdfdcbc894c4e780a5720bd73f83e521837MD51LICENSElicense.txtlicense.txttext/plain; charset=utf-81748https://repositorio.usmp.edu.pe/bitstream/20.500.12727/6206/2/license.txt8a4605be74aa9ea9d79846c1fba20a33MD52TEXTanchelia_rsfmh-2015.pdf.txtanchelia_rsfmh-2015.pdf.txtExtracted texttext/plain19588https://repositorio.usmp.edu.pe/bitstream/20.500.12727/6206/3/anchelia_rsfmh-2015.pdf.txtc4b8fa5faca989e188d9f4a200f00858MD53THUMBNAILanchelia_rsfmh-2015.pdf.jpganchelia_rsfmh-2015.pdf.jpgGenerated Thumbnailimage/jpeg9208https://repositorio.usmp.edu.pe/bitstream/20.500.12727/6206/4/anchelia_rsfmh-2015.pdf.jpg22edff3f4a39eabf5d49ea2b486d0558MD5420.500.12727/6206oai:repositorio.usmp.edu.pe:20.500.12727/62062025-08-15 09:57:23.825REPOSITORIO ACADEMICO USMPrepositorio@usmp.peTk9URTogUExBQ0UgWU9VUiBPV04gTElDRU5TRSBIRVJFClRoaXMgc2FtcGxlIGxpY2Vuc2UgaXMgcHJvdmlkZWQgZm9yIGluZm9ybWF0aW9uYWwgcHVycG9zZXMgb25seS4KCk5PTi1FWENMVVNJVkUgRElTVFJJQlVUSU9OIExJQ0VOU0UKCkJ5IHNpZ25pbmcgYW5kIHN1Ym1pdHRpbmcgdGhpcyBsaWNlbnNlLCB5b3UgKHRoZSBhdXRob3Iocykgb3IgY29weXJpZ2h0Cm93bmVyKSBncmFudHMgdG8gRFNwYWNlIFVuaXZlcnNpdHkgKERTVSkgdGhlIG5vbi1leGNsdXNpdmUgcmlnaHQgdG8gcmVwcm9kdWNlLAp0cmFuc2xhdGUgKGFzIGRlZmluZWQgYmVsb3cpLCBhbmQvb3IgZGlzdHJpYnV0ZSB5b3VyIHN1Ym1pc3Npb24gKGluY2x1ZGluZwp0aGUgYWJzdHJhY3QpIHdvcmxkd2lkZSBpbiBwcmludCBhbmQgZWxlY3Ryb25pYyBmb3JtYXQgYW5kIGluIGFueSBtZWRpdW0sCmluY2x1ZGluZyBidXQgbm90IGxpbWl0ZWQgdG8gYXVkaW8gb3IgdmlkZW8uCgpZb3UgYWdyZWUgdGhhdCBEU1UgbWF5LCB3aXRob3V0IGNoYW5naW5nIHRoZSBjb250ZW50LCB0cmFuc2xhdGUgdGhlCnN1Ym1pc3Npb24gdG8gYW55IG1lZGl1bSBvciBmb3JtYXQgZm9yIHRoZSBwdXJwb3NlIG9mIHByZXNlcnZhdGlvbi4KCllvdSBhbHNvIGFncmVlIHRoYXQgRFNVIG1heSBrZWVwIG1vcmUgdGhhbiBvbmUgY29weSBvZiB0aGlzIHN1Ym1pc3Npb24gZm9yCnB1cnBvc2VzIG9mIHNlY3VyaXR5LCBiYWNrLXVwIGFuZCBwcmVzZXJ2YXRpb24uCgpZb3UgcmVwcmVzZW50IHRoYXQgdGhlIHN1Ym1pc3Npb24gaXMgeW91ciBvcmlnaW5hbCB3b3JrLCBhbmQgdGhhdCB5b3UgaGF2ZQp0aGUgcmlnaHQgdG8gZ3JhbnQgdGhlIHJpZ2h0cyBjb250YWluZWQgaW4gdGhpcyBsaWNlbnNlLiBZb3UgYWxzbyByZXByZXNlbnQKdGhhdCB5b3VyIHN1Ym1pc3Npb24gZG9lcyBub3QsIHRvIHRoZSBiZXN0IG9mIHlvdXIga25vd2xlZGdlLCBpbmZyaW5nZSB1cG9uCmFueW9uZSdzIGNvcHlyaWdodC4KCklmIHRoZSBzdWJtaXNzaW9uIGNvbnRhaW5zIG1hdGVyaWFsIGZvciB3aGljaCB5b3UgZG8gbm90IGhvbGQgY29weXJpZ2h0LAp5b3UgcmVwcmVzZW50IHRoYXQgeW91IGhhdmUgb2J0YWluZWQgdGhlIHVucmVzdHJpY3RlZCBwZXJtaXNzaW9uIG9mIHRoZQpjb3B5cmlnaHQgb3duZXIgdG8gZ3JhbnQgRFNVIHRoZSByaWdodHMgcmVxdWlyZWQgYnkgdGhpcyBsaWNlbnNlLCBhbmQgdGhhdApzdWNoIHRoaXJkLXBhcnR5IG93bmVkIG1hdGVyaWFsIGlzIGNsZWFybHkgaWRlbnRpZmllZCBhbmQgYWNrbm93bGVkZ2VkCndpdGhpbiB0aGUgdGV4dCBvciBjb250ZW50IG9mIHRoZSBzdWJtaXNzaW9uLgoKSUYgVEhFIFNVQk1JU1NJT04gSVMgQkFTRUQgVVBPTiBXT1JLIFRIQVQgSEFTIEJFRU4gU1BPTlNPUkVEIE9SIFNVUFBPUlRFRApCWSBBTiBBR0VOQ1kgT1IgT1JHQU5JWkFUSU9OIE9USEVSIFRIQU4gRFNVLCBZT1UgUkVQUkVTRU5UIFRIQVQgWU9VIEhBVkUKRlVMRklMTEVEIEFOWSBSSUdIVCBPRiBSRVZJRVcgT1IgT1RIRVIgT0JMSUdBVElPTlMgUkVRVUlSRUQgQlkgU1VDSApDT05UUkFDVCBPUiBBR1JFRU1FTlQuCgpEU1Ugd2lsbCBjbGVhcmx5IGlkZW50aWZ5IHlvdXIgbmFtZShzKSBhcyB0aGUgYXV0aG9yKHMpIG9yIG93bmVyKHMpIG9mIHRoZQpzdWJtaXNzaW9uLCBhbmQgd2lsbCBub3QgbWFrZSBhbnkgYWx0ZXJhdGlvbiwgb3RoZXIgdGhhbiBhcyBhbGxvd2VkIGJ5IHRoaXMKbGljZW5zZSwgdG8geW91ciBzdWJtaXNzaW9uLgo= |
| score |
12.804897 |
Nota importante:
La información contenida en este registro es de entera responsabilidad de la institución que gestiona el repositorio institucional donde esta contenido este documento o set de datos. El CONCYTEC no se hace responsable por los contenidos (publicaciones y/o datos) accesibles a través del Repositorio Nacional Digital de Ciencia, Tecnología e Innovación de Acceso Abierto (ALICIA).
La información contenida en este registro es de entera responsabilidad de la institución que gestiona el repositorio institucional donde esta contenido este documento o set de datos. El CONCYTEC no se hace responsable por los contenidos (publicaciones y/o datos) accesibles a través del Repositorio Nacional Digital de Ciencia, Tecnología e Innovación de Acceso Abierto (ALICIA).