In this work a systematic investigation on the effect synthesis of temperature_x000D_ (from 0 to 40°C) and ageing time on the size and width of the energy band gap of_x000D_ ZnO nanoparticles, which have been synthesized by a modified Sol-Gel method, is_x000D_ reported. The optical properties of ZnO nanoparticles have been evaluated by_x000D_ their UV-vis absorption spectra, from which the size and energy band gap were_x000D_ obtained. The average of nanoparticle size ranged from 2.06nm to 6.78nm as the_x000D_ temperature was increased from 0ºC to 40°C, while the band gap decreases from_x000D_ 3.99eV to 3.46eV, respectively. A distribution of nanoparticle particle size also was_x000D_ observed for all temperatures and ageing times

Esta investigación tiene como objetivo establecer los procedimientos de fabricación para obtener materiales con una estructura nanométrica, específicamente micro-nanofibras, que son sintetizadas utilizando materiales semiconductores nanoestructurados en una solución de polímero mediante la técnica electrospinning. Se han examinado las variaciones en las micro-nanofibras debido a la interacción con rayos gamma y/o neutrones, así como las implicaciones de los parámetros clave de la técnica, como el voltaje, la amplitud de trabajo y las dimensiones del inyector, los cuales son cruciales para garantizar la continuidad, homogeneidad y tamaño de las fibras. También se ha investigado las dimensiones y la morfología superficial de las micro-nanofibras poliméricas que contienen nanopartículas semiconductoras, estas últimas producidas mediante el método sol-gel, con el propósito...