"Influencia de la temperatura y la agitación del medio corrosivo constituido por acido sulfamico (h2nso3h-0.5m), sobre la velocidad de corrosión de los aceros astm a335 grado p22, astm a335 grado p91, y astm a213 grado t92, medido mediante diferentes técnicas electroquímicas”

Descripción del Articulo

The corrosion behaviour of ASTM A335 P22, ASTM A335 P91 and ASTM A213 T92 steels, in a solution of H2NSO4H-0.5M at different temperatures (298-338 K) and stirring velocities (0 – 700 rpm) was investigated, using methods: Tafel extrapolation, linear polarization resistance, electrochemical impedance...

Descripción completa

Detalles Bibliográficos
Autor: Cholan Quispe, Miguel Angel
Formato: tesis de grado
Fecha de Publicación:2015
Institución:Universidad Nacional de Trujillo
Repositorio:UNITRU-Tesis
Lenguaje:español
OAI Identifier:oai:dspace.unitru.edu.pe:20.500.14414/10392
Enlace del recurso:https://hdl.handle.net/20.500.14414/10392
Nivel de acceso:acceso abierto
Materia:Velocidad de corrosión del acero
id UNIT_7180a6ccc978bf89b15f8b2ebd85f6c3
oai_identifier_str oai:dspace.unitru.edu.pe:20.500.14414/10392
network_acronym_str UNIT
network_name_str UNITRU-Tesis
repository_id_str 4801
dc.title.es_PE.fl_str_mv "Influencia de la temperatura y la agitación del medio corrosivo constituido por acido sulfamico (h2nso3h-0.5m), sobre la velocidad de corrosión de los aceros astm a335 grado p22, astm a335 grado p91, y astm a213 grado t92, medido mediante diferentes técnicas electroquímicas”
title "Influencia de la temperatura y la agitación del medio corrosivo constituido por acido sulfamico (h2nso3h-0.5m), sobre la velocidad de corrosión de los aceros astm a335 grado p22, astm a335 grado p91, y astm a213 grado t92, medido mediante diferentes técnicas electroquímicas”
spellingShingle "Influencia de la temperatura y la agitación del medio corrosivo constituido por acido sulfamico (h2nso3h-0.5m), sobre la velocidad de corrosión de los aceros astm a335 grado p22, astm a335 grado p91, y astm a213 grado t92, medido mediante diferentes técnicas electroquímicas”
Cholan Quispe, Miguel Angel
Velocidad de corrosión del acero
title_short "Influencia de la temperatura y la agitación del medio corrosivo constituido por acido sulfamico (h2nso3h-0.5m), sobre la velocidad de corrosión de los aceros astm a335 grado p22, astm a335 grado p91, y astm a213 grado t92, medido mediante diferentes técnicas electroquímicas”
title_full "Influencia de la temperatura y la agitación del medio corrosivo constituido por acido sulfamico (h2nso3h-0.5m), sobre la velocidad de corrosión de los aceros astm a335 grado p22, astm a335 grado p91, y astm a213 grado t92, medido mediante diferentes técnicas electroquímicas”
title_fullStr "Influencia de la temperatura y la agitación del medio corrosivo constituido por acido sulfamico (h2nso3h-0.5m), sobre la velocidad de corrosión de los aceros astm a335 grado p22, astm a335 grado p91, y astm a213 grado t92, medido mediante diferentes técnicas electroquímicas”
title_full_unstemmed "Influencia de la temperatura y la agitación del medio corrosivo constituido por acido sulfamico (h2nso3h-0.5m), sobre la velocidad de corrosión de los aceros astm a335 grado p22, astm a335 grado p91, y astm a213 grado t92, medido mediante diferentes técnicas electroquímicas”
title_sort "Influencia de la temperatura y la agitación del medio corrosivo constituido por acido sulfamico (h2nso3h-0.5m), sobre la velocidad de corrosión de los aceros astm a335 grado p22, astm a335 grado p91, y astm a213 grado t92, medido mediante diferentes técnicas electroquímicas”
author Cholan Quispe, Miguel Angel
author_facet Cholan Quispe, Miguel Angel
author_role author
dc.contributor.advisor.fl_str_mv Zavaleta Gutierrez, Nilthon Emerson
dc.contributor.author.fl_str_mv Cholan Quispe, Miguel Angel
dc.subject.es_PE.fl_str_mv Velocidad de corrosión del acero
topic Velocidad de corrosión del acero
description The corrosion behaviour of ASTM A335 P22, ASTM A335 P91 and ASTM A213 T92 steels, in a solution of H2NSO4H-0.5M at different temperatures (298-338 K) and stirring velocities (0 – 700 rpm) was investigated, using methods: Tafel extrapolation, linear polarization resistance, electrochemical impedance spectroscopy and electrochemical frequency modulation The corrosion rate of steel so increased exponentially with temperature. This effect is more pronounced in P22 steel, being the order of corrosion resistance at 338 K (65oC), T92  P91  P22. Likewise, increased stirring results in increased corrosion rate, with greater effect in the P22 steel. Increasing both the temperature and stirring of the acid solution produced on the surface of the steels a depolarization hydrogen evolution reaction. The corrosion rate data obtained with the four techniques evaluated show good agreement. Keywords:
publishDate 2015
dc.date.accessioned.none.fl_str_mv 2018-06-28T15:10:36Z
dc.date.available.none.fl_str_mv 2018-06-28T15:10:36Z
dc.date.issued.fl_str_mv 2015-01
dc.type.es_PE.fl_str_mv info:eu-repo/semantics/bachelorThesis
format bachelorThesis
dc.identifier.uri.none.fl_str_mv https://hdl.handle.net/20.500.14414/10392
url https://hdl.handle.net/20.500.14414/10392
dc.language.iso.es_PE.fl_str_mv spa
language spa
dc.relation.ispartof.fl_str_mv SUNEDU
dc.relation.ispartofseries.none.fl_str_mv Tmt;Tmt
dc.rights.es_PE.fl_str_mv info:eu-repo/semantics/openAccess
dc.rights.uri.es_PE.fl_str_mv http://creativecommons.org/licenses/by-nc-nd/2.5/pe/
eu_rights_str_mv openAccess
rights_invalid_str_mv http://creativecommons.org/licenses/by-nc-nd/2.5/pe/
dc.publisher.es_PE.fl_str_mv Universidad Nacional de Trujillo
dc.source.es_PE.fl_str_mv Universidad Nacional de Trujillo
Repositorio institucional - UNITRU
dc.source.none.fl_str_mv reponame:UNITRU-Tesis
instname:Universidad Nacional de Trujillo
instacron:UNITRU
instname_str Universidad Nacional de Trujillo
instacron_str UNITRU
institution UNITRU
reponame_str UNITRU-Tesis
collection UNITRU-Tesis
bitstream.url.fl_str_mv https://dspace.unitru.edu.pe/bitstreams/b5a7337e-f801-4259-9e4c-21f6e9e06af0/download
https://dspace.unitru.edu.pe/bitstreams/3d229a4b-4adf-4345-a5e8-5880cc49d490/download
bitstream.checksum.fl_str_mv 2cdfe82d2a80165baf9a8b011e0aec66
8a4605be74aa9ea9d79846c1fba20a33
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
repository.name.fl_str_mv Repositorio Institucional - UNITRU
repository.mail.fl_str_mv repositorios@unitru.edu.pe
_version_ 1807290629730861056
spelling Zavaleta Gutierrez, Nilthon EmersonCholan Quispe, Miguel Angel2018-06-28T15:10:36Z2018-06-28T15:10:36Z2015-01https://hdl.handle.net/20.500.14414/10392The corrosion behaviour of ASTM A335 P22, ASTM A335 P91 and ASTM A213 T92 steels, in a solution of H2NSO4H-0.5M at different temperatures (298-338 K) and stirring velocities (0 – 700 rpm) was investigated, using methods: Tafel extrapolation, linear polarization resistance, electrochemical impedance spectroscopy and electrochemical frequency modulation The corrosion rate of steel so increased exponentially with temperature. This effect is more pronounced in P22 steel, being the order of corrosion resistance at 338 K (65oC), T92  P91  P22. Likewise, increased stirring results in increased corrosion rate, with greater effect in the P22 steel. Increasing both the temperature and stirring of the acid solution produced on the surface of the steels a depolarization hydrogen evolution reaction. The corrosion rate data obtained with the four techniques evaluated show good agreement. Keywords:Se investigó el comportamiento a la corrosión de los aceros ASTM A335 P22, ASTM A335 P91 y ASTM A213 T92 en una solución de H2NSO4H-0.5M a diferentes temperaturas (298-338 K) y velocidades de agitación (0 - 700 rpm), utilizando los métodos de extrapolación Tafel, resistencia a la polarización lineal, espectroscopia de impedancia electroquímica y modulación de frecuencia electroquímica. La velocidad de corrosión de los aceros evaluados incrementa de manera exponencial con la temperatura. Este efecto es más pronunciado en acero P22, siendo el orden de la resistencia a la corrosión a 338 K (65ºC), T92  P91  P22. Asimismo, un aumento en la agitación produce un incremento en la velocidad de corrosión, con mayor efecto en el acero P22. Tanto el incremento de la temperatura como de la agitación de la solución ácida, produce en la superficie de los aceros evaluados una despolarización de la reacción de evolución de hidrógeno. Los datos de velocidades de corrosión obtenidos con las cuatro técnicas evaluadas muestran una buena concordancia.TesisspaUniversidad Nacional de TrujilloTmt;TmtSUNEDUinfo:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by-nc-nd/2.5/pe/Universidad Nacional de TrujilloRepositorio institucional - UNITRUreponame:UNITRU-Tesisinstname:Universidad Nacional de Trujilloinstacron:UNITRUVelocidad de corrosión del acero"Influencia de la temperatura y la agitación del medio corrosivo constituido por acido sulfamico (h2nso3h-0.5m), sobre la velocidad de corrosión de los aceros astm a335 grado p22, astm a335 grado p91, y astm a213 grado t92, medido mediante diferentes técnicas electroquímicas”info:eu-repo/semantics/bachelorThesisTítulo ProfesionalIngeniero MetalúrgicoIngenieríaUniversidad Nacional de Trujillo. Facultad de IngenieríaORIGINALCholan Quispe - Ruiz Visalot.pdfCholan Quispe - Ruiz Visalot.pdfVelocidad de corrosión del aceroapplication/pdf7982095https://dspace.unitru.edu.pe/bitstreams/b5a7337e-f801-4259-9e4c-21f6e9e06af0/download2cdfe82d2a80165baf9a8b011e0aec66MD51LICENSElicense.txtlicense.txttext/plain; charset=utf-81748https://dspace.unitru.edu.pe/bitstreams/3d229a4b-4adf-4345-a5e8-5880cc49d490/download8a4605be74aa9ea9d79846c1fba20a33MD5220.500.14414/10392oai:dspace.unitru.edu.pe:20.500.14414/103922018-06-28 10:10:36.784http://creativecommons.org/licenses/by-nc-nd/2.5/pe/info:eu-repo/semantics/openAccessopen.accesshttps://dspace.unitru.edu.peRepositorio Institucional - UNITRUrepositorios@unitru.edu.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
score 13.7211075
"Influencia de la temperatura y la agitación del medio corrosivo constituido por acido sulfamico (h2nso3h-0.5m), sobre la velocidad de corrosión de los aceros astm a335 grado p22, astm a335 grado p91, y astm a213 grado t92, medido mediante diferentes técnicas electroquímicas”
Nota importante:
La información contenida en este registro es de entera responsabilidad de la institución que gestiona el repositorio institucional donde esta contenido este documento o set de datos. El CONCYTEC no se hace responsable por los contenidos (publicaciones y/o datos) accesibles a través del Repositorio Nacional Digital de Ciencia, Tecnología e Innovación de Acceso Abierto (ALICIA).

Ejemplares Similares