Analysis of the physical properties and photoelectrochemical behavior of c-Si/a-SiC:H(p) photocathodes for solar water splitting

Descripción del Articulo

Photoelectrochemical (PEC) processes have become an efficient and viable method for solar energy conversion into zero-emission fuels by harnessing and storage the power of the sun, which offers an environment-friendly approach. Hydrogen is considered as a sustainable and suitable energy alternative...

Descripción completa

Detalles Bibliográficos
Autor: Mejia Chueca, María del Carmen
Formato: tesis doctoral
Fecha de Publicación:2022
Institución:Pontificia Universidad Católica del Perú
Repositorio:PUCP-Tesis
Lenguaje:inglés
OAI Identifier:oai:tesis.pucp.edu.pe:20.500.12404/24006
Enlace del recurso:http://hdl.handle.net/20.500.12404/24006
Nivel de acceso:acceso abierto
Materia:Fotocatálisis
Fotoelectroquímica
Fuentes de energía renovables
https://purl.org/pe-repo/ocde/ford#1.03.00
id PUCP_1ebb157a694cd8c0f3624db597705020
oai_identifier_str oai:tesis.pucp.edu.pe:20.500.12404/24006
network_acronym_str PUCP
network_name_str PUCP-Tesis
repository_id_str .
dc.title.es_ES.fl_str_mv Analysis of the physical properties and photoelectrochemical behavior of c-Si/a-SiC:H(p) photocathodes for solar water splitting
title Analysis of the physical properties and photoelectrochemical behavior of c-Si/a-SiC:H(p) photocathodes for solar water splitting
spellingShingle Analysis of the physical properties and photoelectrochemical behavior of c-Si/a-SiC:H(p) photocathodes for solar water splitting
Mejia Chueca, María del Carmen
Fotocatálisis
Fotoelectroquímica
Fuentes de energía renovables
https://purl.org/pe-repo/ocde/ford#1.03.00
title_short Analysis of the physical properties and photoelectrochemical behavior of c-Si/a-SiC:H(p) photocathodes for solar water splitting
title_full Analysis of the physical properties and photoelectrochemical behavior of c-Si/a-SiC:H(p) photocathodes for solar water splitting
title_fullStr Analysis of the physical properties and photoelectrochemical behavior of c-Si/a-SiC:H(p) photocathodes for solar water splitting
title_full_unstemmed Analysis of the physical properties and photoelectrochemical behavior of c-Si/a-SiC:H(p) photocathodes for solar water splitting
title_sort Analysis of the physical properties and photoelectrochemical behavior of c-Si/a-SiC:H(p) photocathodes for solar water splitting
author Mejia Chueca, María del Carmen
author_facet Mejia Chueca, María del Carmen
author_role author
dc.contributor.advisor.fl_str_mv Rumiche Zapata, Francisco Aurelio
dc.contributor.author.fl_str_mv Mejia Chueca, María del Carmen
dc.subject.es_ES.fl_str_mv Fotocatálisis
Fotoelectroquímica
Fuentes de energía renovables
topic Fotocatálisis
Fotoelectroquímica
Fuentes de energía renovables
https://purl.org/pe-repo/ocde/ford#1.03.00
dc.subject.ocde.none.fl_str_mv https://purl.org/pe-repo/ocde/ford#1.03.00
description Photoelectrochemical (PEC) processes have become an efficient and viable method for solar energy conversion into zero-emission fuels by harnessing and storage the power of the sun, which offers an environment-friendly approach. Hydrogen is considered as a sustainable and suitable energy alternative in comparison to energy systems based on the consumption of conventional hydrocarbon fuels. In particular, hydrogen production by PEC water splitting represents an attractive alternative to enhance the efficiency of water splitting process using sun light. Current research in this field is devoted to the fabrication and evaluation of new photoactive materials that upon sunlight absorption enable water-splitting PEC reactions with high efficiency and durability. Silicon based compounds offer a good opportunity as photoactive material due to its high abundance and current scalable technologies. Silicon is the eighth most abundant element in the universe and constitutes up to 27.2% of the earth’s crust weight [1]. Particularly, hydrogenated amorphous silicon carbide (a-SiC:H) thin films have been tested as photocathode material for photo-assisted electrolysis, exhibiting solar to hydrogen conversion efficiencies up to 7.5 %. Due to the capability to tailor the bandgap (1.8 - 3.3 eV) by the incorporation of carbon in a-Si:H, this material has turned out to be a promising candidate for PEC cells, fulfilling the optical bandgap (Egap) primary requirement, i.e. Egap > 2.2 eV. Additionally, the carbon incorporation leads to an enhancement of the corrosion resistance properties in aqueous media. It has been theoretically estimated that a PEC device with an a-Si0.9C0.1:H absorption layer exhibiting 2.0 eV of energy bandgap, can generate a photocurrent density Jph of 15 mA/cm2 (solar-to-hydrogen conversion efficiency ∼18 %) when submitted to an Air mass (AM) 1.5 solar spectrum [2]. The specific value of 1.5 for the Air mass is selected for standardization purposes, based on the analysis of solar irradiance data in the United States, and corresponds to a power of 1000 W/cm2 [3]. In the present work, a similar material a-Si0.5C0.5:H exhibiting 2.76 eV of energy bandgap generates a Jph of 17 mA/cm2 when submitted to the same light spectrum. This reflects an improvement in the use of a-SiC:H in PEC water splitting. Research on single thin film photoactive materials does not typically consider the role of the silicon substrate in the photoelectrochemical performance. In this sense, the photoelectrode is a system formed by a p-p, n-n or n-p structure, which depending on the depth of the space charge region may have an important impact on the photoelectrode performance. In this work, this substrate effect has been considered and studied. PEC performance of a-SiC:H is often limited by its non-ideal energy band-edge alignment to the H2O/O2 redox potential, thus limiting the oxygen evolution reaction (OER) and the whole water splitting process [4]. To overcome this downside, an external bias needs to be applied, contributing to counteract the overpotential required to trigger the direct water splitting reaction. The external bias also contributes to reduce overpotentials due to the presence of a surface SiO2 barrier layer and compensates interface charge carriers recombination as well. Previous studies have demonstrated that by removing the SiO2 native layer vii from a-SiC:H(i) surface, Jph values over 6 mA/cm2 can be achieved at a potential of -1.4 V vs. Ag/AgCl in contrast to values lower than < 4 mA/cm2 obtained without the oxide removal. In fact, the existence of surface states (SS) originated from the hydroxyl group termination on the oxide surface, form an electronic state that is typically located within the semiconductor bandgap. The theory that such states act as recombination centers for minority photo carriers, fits quite well with the assumption that surface recombination competes with charge transfer from the semiconductor band towards the electrolyte. Additionally, it has been reported that depending on the density and energetic position of SS, these can provide another favorable pathway for indirect charge transfer to the solution, competing with the undesirable recombination mechanism. Knowledge in this field is limitated to full-drift diffusion simulations in steady-state and dynamic regimes for photo-anodic currents in crystalline materials. In the current work, an experimental study has been carried out over an amorphous material (a-SiC:H) acting as photocathode for PEC water splitting. Thus, adding knowledge in this field. Attempts to understand the role of a-SiC defects in PEC water splitting performance have been carried out in 2009 by Simonds et al. [5]. As a result of these, defects density in the bulk of the a-SiC increases with carbon concentration, from ∼9 × 1016 cm−3 (6%C) to ∼8 × 1017 cm−3 (11%C), leading to a reduction of the PEC performance. On the other hand, defect densities in the SiC/SiO2 interface (SS) were approximated by Gaussian distributions with maximums of ∼2 × 1012 cm−2 · eV−1 (Ivanov et al. [6]). The latter finding was retrieved from Capacitance-Voltage (C−V) measurements over metal-oxide-semiconductor (MOS) structures, and fit quite well with the SiC SS density distributions reported in this work. The current work consists in three parts. In the first part, Bandgap engineering of a-SiC:H thin films was carried out to assess the material light absorption without compromising its photoelectrochemical water splitting capabilities. The tailoring was performed by varying the hydrogen concentration in the semiconductor and by post-deposition isochronical annealing treatments from 200 to 700 ◦C. By isochronical annealing, the same sample is submitted to the different temperature steps, from low to high temperature. After this analysis, the most suitable samples for water splitting application were evaluated as photocathodes in 1 M sulfuric acid under chopped light illumination. These a-SiC:H samples were doped with aluminum and deposited on different Silicon substrate conductivity types to assess the substrate influence in the a-SiC:H(Al) photocurrent response. This constitutes the second part or the work. Finally, in the third part, the role of SS in the photocathodic current for a-SiC:H(Al) absorber layers was experimentally analyzed. This analysis was based on steady-state and dynamic electrochemical models. Results concerning a-SiC:H(Al) photocathode stability under darkness and illumination conditions are also shown and discussed in this part. Concerning the findings and the novelty in this work, localized a-SiC:H(Al)/SiO2 SS would take part in a desirable mechanism of indirect electron charge transfer viii to the electrolyte, and thus, conduct hydrogen evolution reaction. Related to the SiO2 native layer, the evidence suggests that the SiO2 layer reduction during PEC tests triggers a favorable semiconductor-electrolyte interface. This interface exhibits less overpotential barriers which promotes photocurrent generation. A correlation exists between the retrieved SS density (NSS) and Urbach energy (EU) values. The EU is associated with disorder-induced electronic tail states or Urbach tails, which are localized states near the semiconductor band-edges. This correlation, as well as other a-SiC:H(Al)/SiO2 interface studies, support the reliability of our NSS calculations for the c-Si(p)/a-SiC:H(Al)/SiO2/electrolyte system. Finally, a charge transfer mechanism assisted by photogenerated minority carriers from the c-Si substrate has been also proposed in this work
publishDate 2022
dc.date.created.none.fl_str_mv 2022
dc.date.accessioned.none.fl_str_mv 2023-01-16T15:03:05Z
dc.date.available.none.fl_str_mv 2023-01-16T15:03:05Z
dc.date.issued.fl_str_mv 2023-01-16
dc.type.es_ES.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
dc.identifier.uri.none.fl_str_mv http://hdl.handle.net/20.500.12404/24006
url http://hdl.handle.net/20.500.12404/24006
dc.language.iso.none.fl_str_mv eng
language eng
dc.relation.ispartof.fl_str_mv SUNEDU
dc.rights.es_ES.fl_str_mv info:eu-repo/semantics/openAccess
dc.rights.uri.*.fl_str_mv http://creativecommons.org/licenses/by/2.5/pe/
eu_rights_str_mv openAccess
rights_invalid_str_mv http://creativecommons.org/licenses/by/2.5/pe/
dc.publisher.es_ES.fl_str_mv Pontificia Universidad Católica del Perú
dc.publisher.country.none.fl_str_mv PE
dc.source.none.fl_str_mv reponame:PUCP-Tesis
instname:Pontificia Universidad Católica del Perú
instacron:PUCP
instname_str Pontificia Universidad Católica del Perú
instacron_str PUCP
institution PUCP
reponame_str PUCP-Tesis
collection PUCP-Tesis
bitstream.url.fl_str_mv https://tesis.pucp.edu.pe/bitstreams/7e852bfa-eba5-4bed-a058-f6d26ab7c61c/download
https://tesis.pucp.edu.pe/bitstreams/e9636a94-9260-4971-9923-7bc4a94808f2/download
https://tesis.pucp.edu.pe/bitstreams/71a73050-616e-4af7-96e2-e8094684a18f/download
https://tesis.pucp.edu.pe/bitstreams/b9e0674d-c3c1-4b15-a648-bd7527160d66/download
https://tesis.pucp.edu.pe/bitstreams/875f99df-3bc6-4954-86c7-be4ec7e5b7f4/download
https://tesis.pucp.edu.pe/bitstreams/c3d760ce-aed9-4d6f-b8c3-ffdfbcd8008d/download
https://tesis.pucp.edu.pe/bitstreams/11315998-15e5-4c8e-8726-d2269da64c15/download
https://tesis.pucp.edu.pe/bitstreams/9d33a976-d92b-43ee-9cd6-1126a204a531/download
https://tesis.pucp.edu.pe/bitstreams/3519130d-f4a2-4fb2-8476-8b38e0b4af66/download
bitstream.checksum.fl_str_mv 30914aa8cf8e51036114bb02af279757
b4585c191fc9f28fd216786974ec9ade
5a4ffbc01f1b5eb70a835dac0d501661
8a4605be74aa9ea9d79846c1fba20a33
919fd19b7a2f1bb3b7bedad7b23268c3
95bc2748fe5559fb1368e11e3935a11b
a554e2d15a41ce835a3c945104bcff13
a554e2d15a41ce835a3c945104bcff13
a554e2d15a41ce835a3c945104bcff13
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
MD5
MD5
MD5
MD5
MD5
MD5
MD5
repository.name.fl_str_mv Repositorio de Tesis PUCP
repository.mail.fl_str_mv raul.sifuentes@pucp.pe
_version_ 1834736897159593984
spelling Rumiche Zapata, Francisco AurelioMejia Chueca, María del Carmen2023-01-16T15:03:05Z2023-01-16T15:03:05Z20222023-01-16http://hdl.handle.net/20.500.12404/24006Photoelectrochemical (PEC) processes have become an efficient and viable method for solar energy conversion into zero-emission fuels by harnessing and storage the power of the sun, which offers an environment-friendly approach. Hydrogen is considered as a sustainable and suitable energy alternative in comparison to energy systems based on the consumption of conventional hydrocarbon fuels. In particular, hydrogen production by PEC water splitting represents an attractive alternative to enhance the efficiency of water splitting process using sun light. Current research in this field is devoted to the fabrication and evaluation of new photoactive materials that upon sunlight absorption enable water-splitting PEC reactions with high efficiency and durability. Silicon based compounds offer a good opportunity as photoactive material due to its high abundance and current scalable technologies. Silicon is the eighth most abundant element in the universe and constitutes up to 27.2% of the earth’s crust weight [1]. Particularly, hydrogenated amorphous silicon carbide (a-SiC:H) thin films have been tested as photocathode material for photo-assisted electrolysis, exhibiting solar to hydrogen conversion efficiencies up to 7.5 %. Due to the capability to tailor the bandgap (1.8 - 3.3 eV) by the incorporation of carbon in a-Si:H, this material has turned out to be a promising candidate for PEC cells, fulfilling the optical bandgap (Egap) primary requirement, i.e. Egap > 2.2 eV. Additionally, the carbon incorporation leads to an enhancement of the corrosion resistance properties in aqueous media. It has been theoretically estimated that a PEC device with an a-Si0.9C0.1:H absorption layer exhibiting 2.0 eV of energy bandgap, can generate a photocurrent density Jph of 15 mA/cm2 (solar-to-hydrogen conversion efficiency ∼18 %) when submitted to an Air mass (AM) 1.5 solar spectrum [2]. The specific value of 1.5 for the Air mass is selected for standardization purposes, based on the analysis of solar irradiance data in the United States, and corresponds to a power of 1000 W/cm2 [3]. In the present work, a similar material a-Si0.5C0.5:H exhibiting 2.76 eV of energy bandgap generates a Jph of 17 mA/cm2 when submitted to the same light spectrum. This reflects an improvement in the use of a-SiC:H in PEC water splitting. Research on single thin film photoactive materials does not typically consider the role of the silicon substrate in the photoelectrochemical performance. In this sense, the photoelectrode is a system formed by a p-p, n-n or n-p structure, which depending on the depth of the space charge region may have an important impact on the photoelectrode performance. In this work, this substrate effect has been considered and studied. PEC performance of a-SiC:H is often limited by its non-ideal energy band-edge alignment to the H2O/O2 redox potential, thus limiting the oxygen evolution reaction (OER) and the whole water splitting process [4]. To overcome this downside, an external bias needs to be applied, contributing to counteract the overpotential required to trigger the direct water splitting reaction. The external bias also contributes to reduce overpotentials due to the presence of a surface SiO2 barrier layer and compensates interface charge carriers recombination as well. Previous studies have demonstrated that by removing the SiO2 native layer vii from a-SiC:H(i) surface, Jph values over 6 mA/cm2 can be achieved at a potential of -1.4 V vs. Ag/AgCl in contrast to values lower than < 4 mA/cm2 obtained without the oxide removal. In fact, the existence of surface states (SS) originated from the hydroxyl group termination on the oxide surface, form an electronic state that is typically located within the semiconductor bandgap. The theory that such states act as recombination centers for minority photo carriers, fits quite well with the assumption that surface recombination competes with charge transfer from the semiconductor band towards the electrolyte. Additionally, it has been reported that depending on the density and energetic position of SS, these can provide another favorable pathway for indirect charge transfer to the solution, competing with the undesirable recombination mechanism. Knowledge in this field is limitated to full-drift diffusion simulations in steady-state and dynamic regimes for photo-anodic currents in crystalline materials. In the current work, an experimental study has been carried out over an amorphous material (a-SiC:H) acting as photocathode for PEC water splitting. Thus, adding knowledge in this field. Attempts to understand the role of a-SiC defects in PEC water splitting performance have been carried out in 2009 by Simonds et al. [5]. As a result of these, defects density in the bulk of the a-SiC increases with carbon concentration, from ∼9 × 1016 cm−3 (6%C) to ∼8 × 1017 cm−3 (11%C), leading to a reduction of the PEC performance. On the other hand, defect densities in the SiC/SiO2 interface (SS) were approximated by Gaussian distributions with maximums of ∼2 × 1012 cm−2 · eV−1 (Ivanov et al. [6]). The latter finding was retrieved from Capacitance-Voltage (C−V) measurements over metal-oxide-semiconductor (MOS) structures, and fit quite well with the SiC SS density distributions reported in this work. The current work consists in three parts. In the first part, Bandgap engineering of a-SiC:H thin films was carried out to assess the material light absorption without compromising its photoelectrochemical water splitting capabilities. The tailoring was performed by varying the hydrogen concentration in the semiconductor and by post-deposition isochronical annealing treatments from 200 to 700 ◦C. By isochronical annealing, the same sample is submitted to the different temperature steps, from low to high temperature. After this analysis, the most suitable samples for water splitting application were evaluated as photocathodes in 1 M sulfuric acid under chopped light illumination. These a-SiC:H samples were doped with aluminum and deposited on different Silicon substrate conductivity types to assess the substrate influence in the a-SiC:H(Al) photocurrent response. This constitutes the second part or the work. Finally, in the third part, the role of SS in the photocathodic current for a-SiC:H(Al) absorber layers was experimentally analyzed. This analysis was based on steady-state and dynamic electrochemical models. Results concerning a-SiC:H(Al) photocathode stability under darkness and illumination conditions are also shown and discussed in this part. Concerning the findings and the novelty in this work, localized a-SiC:H(Al)/SiO2 SS would take part in a desirable mechanism of indirect electron charge transfer viii to the electrolyte, and thus, conduct hydrogen evolution reaction. Related to the SiO2 native layer, the evidence suggests that the SiO2 layer reduction during PEC tests triggers a favorable semiconductor-electrolyte interface. This interface exhibits less overpotential barriers which promotes photocurrent generation. A correlation exists between the retrieved SS density (NSS) and Urbach energy (EU) values. The EU is associated with disorder-induced electronic tail states or Urbach tails, which are localized states near the semiconductor band-edges. This correlation, as well as other a-SiC:H(Al)/SiO2 interface studies, support the reliability of our NSS calculations for the c-Si(p)/a-SiC:H(Al)/SiO2/electrolyte system. Finally, a charge transfer mechanism assisted by photogenerated minority carriers from the c-Si substrate has been also proposed in this workengPontificia Universidad Católica del PerúPEinfo:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by/2.5/pe/FotocatálisisFotoelectroquímicaFuentes de energía renovableshttps://purl.org/pe-repo/ocde/ford#1.03.00Analysis of the physical properties and photoelectrochemical behavior of c-Si/a-SiC:H(p) photocathodes for solar water splittinginfo:eu-repo/semantics/doctoralThesisreponame:PUCP-Tesisinstname:Pontificia Universidad Católica del Perúinstacron:PUCPSUNEDUDoctor en FísicaDoctoradoPontificia Universidad Católica del Perú. Escuela de PosgradoFísica10491814http://orcid.org/0000-0001-9318-842546472788533018Guerra Torres, Jorge AndresRumiche Zapata, Francisco AurelioBund, Andreashttps://purl.org/pe-repo/renati/level#doctorhttps://purl.org/pe-repo/renati/type#tesisORIGINALMEJÍA_CHUECA_MARIA DEL CARMEN_ANALYSIS_PHYSICAL_PROPERTIES.pdfMEJÍA_CHUECA_MARIA DEL CARMEN_ANALYSIS_PHYSICAL_PROPERTIES.pdfTexto completoapplication/pdf10235467https://tesis.pucp.edu.pe/bitstreams/7e852bfa-eba5-4bed-a058-f6d26ab7c61c/download30914aa8cf8e51036114bb02af279757MD51trueAnonymousREADMEJÍA_CHUECA_MARIA DEL CARMEN_T.pdfMEJÍA_CHUECA_MARIA DEL CARMEN_T.pdfReporte de originalidadapplication/pdf24365012https://tesis.pucp.edu.pe/bitstreams/e9636a94-9260-4971-9923-7bc4a94808f2/downloadb4585c191fc9f28fd216786974ec9adeMD52falseAnonymousREAD2500-01-01CC-LICENSElicense_rdflicense_rdfapplication/rdf+xml; charset=utf-8914https://tesis.pucp.edu.pe/bitstreams/71a73050-616e-4af7-96e2-e8094684a18f/download5a4ffbc01f1b5eb70a835dac0d501661MD53falseAnonymousREADLICENSElicense.txtlicense.txttext/plain; charset=utf-81748https://tesis.pucp.edu.pe/bitstreams/b9e0674d-c3c1-4b15-a648-bd7527160d66/download8a4605be74aa9ea9d79846c1fba20a33MD54falseAnonymousREADTHUMBNAILMEJÍA_CHUECA_MARIA DEL CARMEN_ANALYSIS_PHYSICAL_PROPERTIES.pdf.jpgMEJÍA_CHUECA_MARIA DEL CARMEN_ANALYSIS_PHYSICAL_PROPERTIES.pdf.jpgIM Thumbnailimage/jpeg12240https://tesis.pucp.edu.pe/bitstreams/875f99df-3bc6-4954-86c7-be4ec7e5b7f4/download919fd19b7a2f1bb3b7bedad7b23268c3MD55falseAnonymousREADMEJÍA_CHUECA_MARIA DEL CARMEN_T.pdf.jpgMEJÍA_CHUECA_MARIA DEL CARMEN_T.pdf.jpgIM Thumbnailimage/jpeg6426https://tesis.pucp.edu.pe/bitstreams/c3d760ce-aed9-4d6f-b8c3-ffdfbcd8008d/download95bc2748fe5559fb1368e11e3935a11bMD56falseAnonymousREAD2500-01-01TEXTMEJÍA_CHUECA_MARIA DEL CARMEN_T.pdf.txtMEJÍA_CHUECA_MARIA DEL CARMEN_T.pdf.txtExtracted texttext/plain26829https://tesis.pucp.edu.pe/bitstreams/11315998-15e5-4c8e-8726-d2269da64c15/downloada554e2d15a41ce835a3c945104bcff13MD57falseAnonymousREAD2500-01-01TEXTMEJÍA_CHUECA_MARIA DEL CARMEN_T.pdf.txtMEJÍA_CHUECA_MARIA DEL CARMEN_T.pdf.txtExtracted texttext/plain26829https://tesis.pucp.edu.pe/bitstreams/9d33a976-d92b-43ee-9cd6-1126a204a531/downloada554e2d15a41ce835a3c945104bcff13MD57falseAnonymousREAD2500-01-01TEXTMEJÍA_CHUECA_MARIA DEL CARMEN_T.pdf.txtMEJÍA_CHUECA_MARIA DEL CARMEN_T.pdf.txtExtracted texttext/plain26829https://tesis.pucp.edu.pe/bitstreams/3519130d-f4a2-4fb2-8476-8b38e0b4af66/downloada554e2d15a41ce835a3c945104bcff13MD57falseAnonymousREAD2500-01-0120.500.12404/24006oai:tesis.pucp.edu.pe:20.500.12404/240062025-04-21 11:17:13.808http://creativecommons.org/licenses/by/2.5/pe/info:eu-repo/semantics/openAccessopen.accesshttps://tesis.pucp.edu.peRepositorio de Tesis PUCPraul.sifuentes@pucp.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
score 13.871978
Nota importante:
La información contenida en este registro es de entera responsabilidad de la institución que gestiona el repositorio institucional donde esta contenido este documento o set de datos. El CONCYTEC no se hace responsable por los contenidos (publicaciones y/o datos) accesibles a través del Repositorio Nacional Digital de Ciencia, Tecnología e Innovación de Acceso Abierto (ALICIA).