Influencia de las fibras en el Shotcrete en su capacidad de absorción de energía y resistencia a la flexión
Descripción del Articulo
A la Universidad Nacional de San Agustín de Arequipa (UNSA) por el financiamiento a través del convenio CIENCIACTIVA – UNSA, según contrato de subvención N° 149 – 2016 - UNSA “TESIS PARA OPTAR EL TITULO PROFESIONAL UNSA” A Cienciactiva y Concytec por el apoyo en la gestión del proyecto....
| Autores: | , |
|---|---|
| Formato: | tesis de grado |
| Fecha de Publicación: | 2017 |
| Institución: | Consejo Nacional de Ciencia Tecnología e Innovación |
| Repositorio: | CONCYTEC-Institucional |
| Lenguaje: | español |
| OAI Identifier: | oai:repositorio.concytec.gob.pe:20.500.12390/1922 |
| Enlace del recurso: | https://hdl.handle.net/20.500.12390/1922 |
| Nivel de acceso: | acceso abierto |
| Materia: | Reforzado con fibra Fibras sintéticas https://purl.org/pe-repo/ocde/ford#2.01.01 |
| id |
CONC_26c7b11b7df91aba082b83790a26db1b |
|---|---|
| oai_identifier_str |
oai:repositorio.concytec.gob.pe:20.500.12390/1922 |
| network_acronym_str |
CONC |
| network_name_str |
CONCYTEC-Institucional |
| repository_id_str |
4689 |
| dc.title.none.fl_str_mv |
Influencia de las fibras en el Shotcrete en su capacidad de absorción de energía y resistencia a la flexión |
| title |
Influencia de las fibras en el Shotcrete en su capacidad de absorción de energía y resistencia a la flexión |
| spellingShingle |
Influencia de las fibras en el Shotcrete en su capacidad de absorción de energía y resistencia a la flexión Aragon Quispe, Miguel Angel Reforzado con fibra Fibras sintéticas https://purl.org/pe-repo/ocde/ford#2.01.01 |
| title_short |
Influencia de las fibras en el Shotcrete en su capacidad de absorción de energía y resistencia a la flexión |
| title_full |
Influencia de las fibras en el Shotcrete en su capacidad de absorción de energía y resistencia a la flexión |
| title_fullStr |
Influencia de las fibras en el Shotcrete en su capacidad de absorción de energía y resistencia a la flexión |
| title_full_unstemmed |
Influencia de las fibras en el Shotcrete en su capacidad de absorción de energía y resistencia a la flexión |
| title_sort |
Influencia de las fibras en el Shotcrete en su capacidad de absorción de energía y resistencia a la flexión |
| author |
Aragon Quispe, Miguel Angel |
| author_facet |
Aragon Quispe, Miguel Angel Cornejo Mamani, Mitward Paul |
| author_role |
author |
| author2 |
Cornejo Mamani, Mitward Paul |
| author2_role |
author |
| dc.contributor.author.fl_str_mv |
Aragon Quispe, Miguel Angel Cornejo Mamani, Mitward Paul |
| dc.subject.none.fl_str_mv |
Reforzado con fibra |
| topic |
Reforzado con fibra Fibras sintéticas https://purl.org/pe-repo/ocde/ford#2.01.01 |
| dc.subject.es_PE.fl_str_mv |
Fibras sintéticas |
| dc.subject.ocde.none.fl_str_mv |
https://purl.org/pe-repo/ocde/ford#2.01.01 |
| description |
A la Universidad Nacional de San Agustín de Arequipa (UNSA) por el financiamiento a través del convenio CIENCIACTIVA – UNSA, según contrato de subvención N° 149 – 2016 - UNSA “TESIS PARA OPTAR EL TITULO PROFESIONAL UNSA” A Cienciactiva y Concytec por el apoyo en la gestión del proyecto. |
| publishDate |
2017 |
| dc.date.accessioned.none.fl_str_mv |
2024-05-30T23:13:38Z |
| dc.date.available.none.fl_str_mv |
2024-05-30T23:13:38Z |
| dc.date.issued.fl_str_mv |
2017 |
| dc.type.none.fl_str_mv |
info:eu-repo/semantics/bachelorThesis |
| format |
bachelorThesis |
| dc.identifier.uri.none.fl_str_mv |
https://hdl.handle.net/20.500.12390/1922 |
| url |
https://hdl.handle.net/20.500.12390/1922 |
| dc.language.iso.none.fl_str_mv |
spa |
| language |
spa |
| dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess |
| dc.rights.uri.none.fl_str_mv |
https://creativecommons.org/licenses/by-nc-nd/4.0/ |
| eu_rights_str_mv |
openAccess |
| rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc-nd/4.0/ |
| dc.publisher.none.fl_str_mv |
Universidad Nacional de San Agustín de Arequipa |
| publisher.none.fl_str_mv |
Universidad Nacional de San Agustín de Arequipa |
| dc.source.none.fl_str_mv |
reponame:CONCYTEC-Institucional instname:Consejo Nacional de Ciencia Tecnología e Innovación instacron:CONCYTEC |
| instname_str |
Consejo Nacional de Ciencia Tecnología e Innovación |
| instacron_str |
CONCYTEC |
| institution |
CONCYTEC |
| reponame_str |
CONCYTEC-Institucional |
| collection |
CONCYTEC-Institucional |
| repository.name.fl_str_mv |
Repositorio Institucional CONCYTEC |
| repository.mail.fl_str_mv |
repositorio@concytec.gob.pe |
| _version_ |
1839175395265478656 |
| spelling |
Publicationrp04917600rp04919600Aragon Quispe, Miguel AngelCornejo Mamani, Mitward Paul2024-05-30T23:13:38Z2024-05-30T23:13:38Z2017https://hdl.handle.net/20.500.12390/1922A la Universidad Nacional de San Agustín de Arequipa (UNSA) por el financiamiento a través del convenio CIENCIACTIVA – UNSA, según contrato de subvención N° 149 – 2016 - UNSA “TESIS PARA OPTAR EL TITULO PROFESIONAL UNSA” A Cienciactiva y Concytec por el apoyo en la gestión del proyecto.The fiber reinforced shotcrete in our country has its main application in the mining sector, the lack of national standards and guidelines, coupled with poor experimental research has resulted in the benefits that can be achieved from fiber reinforced shotcrete are not fully exploited. This thesis contributes to filling the experimental gap and serves as a basis for the formulation of national standards and guidelines for fiber reinforced shotcrete. The methodology consisted of a pattern design of wet shotcrete without fiber, then designs in which only the fiber dose was varied, designs were made with 10 kg, 20 kg, 30 kg, 40 kg of metallic fiber per cubic meter of concrete and 2 kg, 4 kg, 6 kg and 8 kg of synthetic fiber per cubic meter of concrete. The influence of the fibers in the shotcrete was determined in the workability (ASTM C143), in the compressive strength obtained by 30 tests of cylindrical cores of concrete extracted with diamond of shotcrete panels (ASTM C42), in the flexural strength measured Indirectly through 30 sawn beams of shotcrete panels (EN 14488-3) and energy absorption of 30 square panels according to the European standard (EN 14488-5) and 30 circular panels according to American standard (ASTM C1550). The results showed that the metallic fibers in the shotcrete had a better structural behavior in the deterioration of the resistance than the synthetic fibers, although the same values of absorbed energy and flexural strength were obtained using synthetic fiber at a lower cost.Consejo Nacional de Ciencia, Tecnología e Innovación Tecnológica - ConcytecspaUniversidad Nacional de San Agustín de Arequipainfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-nd/4.0/Reforzado con fibraFibras sintéticas-1https://purl.org/pe-repo/ocde/ford#2.01.01-1Influencia de las fibras en el Shotcrete en su capacidad de absorción de energía y resistencia a la flexióninfo:eu-repo/semantics/bachelorThesisreponame:CONCYTEC-Institucionalinstname:Consejo Nacional de Ciencia Tecnología e Innovacióninstacron:CONCYTEC20.500.12390/1922oai:repositorio.concytec.gob.pe:20.500.12390/19222024-05-30 16:05:42.209https://creativecommons.org/licenses/by-nc-nd/4.0/info:eu-repo/semantics/openAccesshttp://purl.org/coar/access_right/c_14cbinfo:eu-repo/semantics/closedAccessmetadata only accesshttps://repositorio.concytec.gob.peRepositorio Institucional CONCYTECrepositorio@concytec.gob.pe#PLACEHOLDER_PARENT_METADATA_VALUE##PLACEHOLDER_PARENT_METADATA_VALUE#<Publication xmlns="https://www.openaire.eu/cerif-profile/1.1/" id="052ca3d4-ce02-4cb7-8149-ad0509a0e417"> <Type xmlns="https://www.openaire.eu/cerif-profile/vocab/COAR_Publication_Types">http://purl.org/coar/resource_type/c_1843</Type> <Language>spa</Language> <Title>Influencia de las fibras en el Shotcrete en su capacidad de absorción de energía y resistencia a la flexión</Title> <PublishedIn> <Publication> </Publication> </PublishedIn> <PublicationDate>2017</PublicationDate> <Authors> <Author> <DisplayName>Aragon Quispe, Miguel Angel</DisplayName> <Person id="rp04917" /> <Affiliation> <OrgUnit> </OrgUnit> </Affiliation> </Author> <Author> <DisplayName>Cornejo Mamani, Mitward Paul</DisplayName> <Person id="rp04919" /> <Affiliation> <OrgUnit> </OrgUnit> </Affiliation> </Author> </Authors> <Editors> </Editors> <Publishers> <Publisher> <DisplayName>Universidad Nacional de San Agustín de Arequipa</DisplayName> <OrgUnit /> </Publisher> </Publishers> <License>https://creativecommons.org/licenses/by-nc-nd/4.0/</License> <Keyword>Reforzado con fibra</Keyword> <Keyword>Fibras sintéticas</Keyword> <Abstract>The fiber reinforced shotcrete in our country has its main application in the mining sector, the lack of national standards and guidelines, coupled with poor experimental research has resulted in the benefits that can be achieved from fiber reinforced shotcrete are not fully exploited. This thesis contributes to filling the experimental gap and serves as a basis for the formulation of national standards and guidelines for fiber reinforced shotcrete. The methodology consisted of a pattern design of wet shotcrete without fiber, then designs in which only the fiber dose was varied, designs were made with 10 kg, 20 kg, 30 kg, 40 kg of metallic fiber per cubic meter of concrete and 2 kg, 4 kg, 6 kg and 8 kg of synthetic fiber per cubic meter of concrete. The influence of the fibers in the shotcrete was determined in the workability (ASTM C143), in the compressive strength obtained by 30 tests of cylindrical cores of concrete extracted with diamond of shotcrete panels (ASTM C42), in the flexural strength measured Indirectly through 30 sawn beams of shotcrete panels (EN 14488-3) and energy absorption of 30 square panels according to the European standard (EN 14488-5) and 30 circular panels according to American standard (ASTM C1550). The results showed that the metallic fibers in the shotcrete had a better structural behavior in the deterioration of the resistance than the synthetic fibers, although the same values of absorbed energy and flexural strength were obtained using synthetic fiber at a lower cost.</Abstract> <Access xmlns="http://purl.org/coar/access_right" > </Access> </Publication> -1 |
| score |
13.439101 |
Nota importante:
La información contenida en este registro es de entera responsabilidad de la institución que gestiona el repositorio institucional donde esta contenido este documento o set de datos. El CONCYTEC no se hace responsable por los contenidos (publicaciones y/o datos) accesibles a través del Repositorio Nacional Digital de Ciencia, Tecnología e Innovación de Acceso Abierto (ALICIA).
La información contenida en este registro es de entera responsabilidad de la institución que gestiona el repositorio institucional donde esta contenido este documento o set de datos. El CONCYTEC no se hace responsable por los contenidos (publicaciones y/o datos) accesibles a través del Repositorio Nacional Digital de Ciencia, Tecnología e Innovación de Acceso Abierto (ALICIA).