Stability of the austenitic phase, the hardness variation of manganese steels affected by heat and subjected to impacts

• Autor: Heredia, Juan Carlos
• Formato: artículo
• Fecha de Publicación: 2012
• Institución: Universidad Nacional Mayor de San Marcos
• Repositorio: Revista UNMSM - IIGEO
• Lenguaje: español
• OAI Identifier: oai:ojs.csi.unmsm:article/2285
• Enlace del recurso: https://revistasinvestigacion.unmsm.edu.pe/index.php/iigeo/article/view/2285
• Nivel de acceso: acceso abierto
• Materia: Phase; austenite; Temple; Hadfield Steels; Metallography; Manganese; Fase; Austenita; Aceros Hadfield; Metalografía; Manganeso

In the present investigation the influence of heat is evaluated in the stability of the austenite phase of type Hadfield manganese steel with 12% manganese. The metallographic analysis and hardness testing takes place in specimens of ASTM A128 Grade Cast Steel E-1, in a state of hardening (austenitizing), and with different heating temperatures from 100 ° C, 200 ° C, 300 ° C, 400 ° C and 500 ° C. The results allow us to check and set the maximum temperatures in the austenitic matrix is stable and maintains its excellent mechanical properties.
En el presente trabajo de investigación se evalúa la influencia del calor en la estabilidad de la fase austenítica de los aceros al manganeso tipo Hadfield, con 12% manganeso. El análisis metalográfico y las pruebas de dureza se desarrolla en probetas de acero fundido ASTM A128 Grado E-1, en estado de temple (austenizado), y con diferentes temperaturas de calentamiento, desde 100 °C, 200 °C, 300 °C, 400 °C y 500 °C. Los resultados nos permitirán comprobar y establecer las máximas temperaturas en que la matriz austenítica es estable y mantenga sus excelentes propiedades mecánicas.