The present study proposes an alternative to the use of petroleum materials and vegetal lignocellulosic forest materials to manufacture of secondary packages. Boxes were made with fibers obtained from banana and coconut, agglutinated with rice. Firstly, it was evaluate the amount of water soluble solids was evaluated in the stream, a characteristic that showed significant differences, and of starch, where there were no statistical differences. Subsequently, agglomerates of the rice variety INIAP 15 and the vegetal fibers were elaborated in two different percentages of composition for each type of fiber. Where there were evaluate of density, tension and resistance. Coconut-fiber and banana-based agglomerates reached the highest values in the three physical characteristics evaluated, unlike the agglomerate made from sugarcane, which was eventually discarded as an alternative material in th...

El presente estudio propone una alternativa a la utilización de materiales de petróleo y lignocelulósicos vegetales de origen forestal para la elaboración de empaques secundarios. Se fabricaron cajas con fibras obtenidas del banano y coco, aglutinadas con arrocillo. Primeramente, fueron evaluadas las características del arrocillo de 3 variedades comerciales producidas en Ecuador en cuanto a la cantidad de sólidos hidrosolubles, característica que presentó diferencias significativas, y contenidos de almidón, donde no hubo diferencias estadísticas. Posteriormente, se elaboraron aglomerados de la variedad de arrocillo INIAP 15 y las fibras vegetales en dos diferentes porcentajes de composición para cada tipo de fibra; en dónde se evaluaron características físicas de densidad, tensión y resistencia. Los aglomerados a base de fibra de coco y de banano alcanzaron los valores alt...

This study proposes an alternative biodegradable material for use with lettuce crops utilizing the bare-root hydroponic system, with the aim of functionally replacing expanded polystyrene, commonly used as a supporting material despite being a highly contaminating substance. This proposal is based on the production of individual pieces of floating material made from agro-industrial waste with an organic wax waterproof coating. The materials were produced in Quito, Ecuador, and the variables analyzed were hardness, compressive strength, flexural strength and microbiological contamination of the material during the vegetable growing period. Results showed that the alternative substrate with the greatest adaptability to the crops was made from a carnauba wax-coated palm fiber (Elaeis guineensis) blended with rice, in a ratio of 70%-30%, respectively.

La presente investigación propone una alternativa de material biodegradable para uso en cultivos en medios hidropónicos de lechuga mediante el sistema de producción a raíz desnuda, con el objetivo de sustituir funcionalmente al poliestireno expandido, utilizado de manera habitual como material de soporte, a pesar de ser un elemento altamente contaminante. La propuesta tiene base en la elaboración de módulos individuales de material flotante a partir de desechos agroindustriales con un recubrimiento impermeabilizante de cera orgánica. Los materiales fueron elaborados en la ciudad de Quito, Ecuador, y las variables evaluadas fueron: dureza de superficies, resistencia a la compresión y a la flexión, y contaminación microbiológica del material durante el tiempo de cultivo del vegetal. Como resultado, se obtuvo que la propuesta con mayor adaptabilidad al cultivo fue la elaborada a ...