The presence of contaminants such as arsenic and antimony in polymetallic concentrates can lead to economic losses due to penalties imposed in commercialization contracts when the permissible limits are exceeded. For this reason, the present study focuses on supporting the reduction of these contaminants through the application of alkaline leaching using NaOH and Na2S in polymetallic concentrates. Optical microscopy tests indicated the presence of species with a high content of arsenic and antimony known as gray coppers and silver sulfosalts. Based on the mineralogical characterization, it was possible to solubilize 93.79% of arsenic and 96.21% of antimony, in a time of four hours, at a temperature of 100°C, with a dosage of 48 kg/TM of sodium hydroxide and 13 kg/TM of sodium sulfide, at a granulometry of 10% - 37μ. It was achieved to reduce the arsenic grade to 0.45% and the antimony ...

Caracteriza el concentrado de cobre de la mina Pasto Bueno para la lixiviación alcalina y reducir el contenido de arsénico y antimonio. El estudio se desarrolla ante la necesidad de darle viabilidad técnica - económica al procesamiento de minerales con alto contenido de contaminantes tipo arsénico y antimonio en la unidad minera Pasto bueno, ubicada en el departamento de Áncash, Perú, para lo cual se toma muestras de concentrado de cobre, cuyo análisis químico reporta 22.85% de Cobre, 74.3 Oz/TC de plata, 20.78% de plomo, 10.50% de zinc, 0.57% de bismuto, 7.25% de arsénico y 6.33% de antimonio. Se realiza pruebas metalúrgicas de lixiviación alcalina con Na2S y NaOH, evaluando dicho proceso a las temperaturas de 25, 50, 75 y 100°C, en 120 minutos, cuyos resultados demuestran que a 100 °C se lixivió 67.31% de arsénico y 69.52% de antimonio, con una dosificación de 16.5 Kg/...