Objective: To evaluate the flexural strength of three dental resin cements. Materials and methods: Sixty bars measuring 25x2x2 mm were made of RelyX-U200, RelyxTM Universal and Duo-Link Universal cements. These bars were divided into 3 groups according to brand (n=20) and were kept in distilled water for 24 hours at 37ºC. The 3-point bending test was carried out, according to ISO 4049, in a universal testing machine at a speed of 0.5 mm/min until fracture. Statistical analysis was performed with the Python statistical package, using the one-way Anova test and Tukey's multiple comparisons test with a confidence level of 95%. Results: Duo-Link Universal cement obtained the highest average with respect to flexural strength (104.7±7.8 MPa). Statistically significant differences were found between the three groups (p< 0.001). These differences were present between RelyxTM Universal - Duo...