The present work aimed to characterize the microstructure of the icosahedral phase (ɸ-quasicrystalline phase) of the system with stoichiometric composition of the quasicrystal Al63Cu25Fe12. The ternary alloy with nominal composition of Al63Cu25Fe12 was processed by Mechanical Alloying (MA) as a viable solid state processing method for producing various metastable and stable quasicrystalline phases. The structural characterization of the obtained samples was performed by X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM), while the elemental composition of the chemical elements Al, Fe and Cu were determined by the technique of X-ray spectroscopy by dispersive energy (EDS). According to the results of XRD, the diffraction patterns of Al63Cu25Fe12 showed the presence of β-Al (Fe, Cu) and λ-Al13Fe4 phases coexist with the thermodynamic ɸ-phase quasicrystalline. Finally, eleme...

Este estudio investiga el efecto de la cinética de molienda en la formación de la fase amorfa en la aleación Co65Nb25B10 sintetizada por aleación mecánica de polvos elementales de Co, Nb y B en un molino de bolas planetario de alta energía. Se realizaron caracterizaciones estructurales y magnéticas mediante difracción de rayos X (DRX), microscopía electrónica de barrido (MEB), calorimetría diferencial de barrido (DSC) y magnetometría de muestra vibrante (VSM). Los resultados indican que la molienda a $300$~ rpm durante $15$~ h induce efectivamente la amorfización, atribuida a la acumulación de defectos reticulares y una deformación plástica severa. El análisis térmico demostró la alta estabilidad térmica de la fase amorfa, con una temperatura de inicio de la cristalización (T$_x$) de aproximadamente 725°C y una temperatura de transición vítrea (T$_g$) cercana a 69...