In this work we report the structural and electronic properties of the compound [Y0.8Ca0.2](Ba0.5Sr0.5)2Cu3O7-δ (YCaBaSr) which is a superconductor below the critical temperature TC = 80 K. This compound was prepared using the Sol-Gel method. The structural properties were studied by X-ray diffraction and electronic properties were studied by X-ray Photoemission Spectroscopy (XPS). The results were compared with those ones of the traditional superconductor YBa2Cu3O7-δ (YBCO). The X-ray photoemission spectra were taken at room temperature (normal state) and at 30 K (superconductor state). In the superconductor state, the X-ray photoemission spectra showed a shift in the O 1s. While the position of the Cu3p principal peaks do not change when measuring at 30 K. However, the spectra reveal the appearance of a new peak due to de hybridization of the Cu3d and O2p states. In addition, the Fou...

En este trabajo se reporta las propiedades estructurales y electrónicas del compuesto [Y0.8Ca0.2](Ba0.5Sr0.5)2Cu3O7-δ (YCaBaSr) que es superconductor con temperatura crítica TC = 80 K. El compuesto fue preparado mediante el método Sol-Gel. Las propiedades estructurales y electrónicas de este compuesto se estudiaron mediante difracción de rayos X (DRX) y espectroscopia de fotoemisión de rayos X (XPS) respectivamente. Los resultados fueron comparados con los del superconductor tradicional YBa2Cu3O7- δ (YBCO). Las medidas por XPS se realizaron a temperatura ambiente (en el estado normal) y a 30 K (estado superconductor). En el estado superconductor, los espectros XPS de ambos compuestos muestran corrimiento en el pico O 1s. Mientras que, la posición de los picos principales del Cu 3p no cambian de posición al ser medidos a 30 K y 293 K. Sin embargo, se observa en el espectro la ap...