OBJETIVO: Comparar la microdureza de cuatro cementos resonosos de uso odontológico teniendo en cuenta que existe correlación entre esta propiedad mecánica y el comportamiento clínico del material de cementación. MATERIALES Y MÉTODOS: Se confeccionaron seis cuerpos de prueba para cada cemento evaluado: RelyX™ ARC (3M ESPE) = Gl, Multilink® (IVOCLAR VIVADENT) = G2, MaxCem Elite™ (KERR CORPORATION) = G3 y RelyX™ U200 (3M ESPE) = G4, los que fueron almacenados durante 48 horas a temperatura ambiente y sometidos al ensayo de Microdureza Vickers (VHN) con 200 g-f durante 10 segundos.

El objetivo de este estudio fue comparar el grado de conversión (GC) de cuatro cementos resinosos fotoactivados a través de un disco de disilicato de litio medido en dos tiempos: inicial y a las 24 horas.

Objetivo: Evaluar la tensión compresiva en segundas premolares superiores rehabilitadas con coronas de disilicato de litio (D.L) y de Silicato de litio reforzado con zirconio (S.L) mediante el método de elementos finitos. Metodología: Se construyeron dos modelos virtuales usando el programa Solidworks 2014 para la construcción de modelos. En el primer modelo se representó la dentina remanente, cofia de disilicato de litio, cemento relyx U 200 y porcelana cerámica feldespática IPS e.Max (Ivoclar Vivadent) (MEF 1). En el segundo modelo se representó la dentina remanente, cofia de vita suprinity, cemento relyx U 200 y porcelana (MEF 2). Ambos modelos fueron sometidos a una carga de 200 N. Resultados: El valor de máxima tensión en la corona de disilicato de litio (MEF 1) fue de 166.98 Mpa, mientras que en la corona de Silicato de litio (MEF 2) fue de 177.6 Mpa. El valor de máxima ...

Objetivo: Comparar la microfiltración marginal de carillas oclusales de cerómero con diferentes terminaciones: hombro, chámfer y un grupo control sin preparación. Materiales y métodos: Se utilizaron 33 dientes premolares humanos, sanos, extraídos por indicación de ortodoncia. Se dividieron en tres grupos de once por aleatorización. Una vez cementadas las carillas oclusales, las muestras fueron sometidas a un termociclado manual de 1000 ciclos, con el fin de simular el ambiente de la cavidad bucal. Después, fueron puestas en inmersión pasiva con azul de metileno al 2% por un periodo de 24 horas. Una vez culminado el tiempo, se procedió al corte de las muestras a nivel del surcocentral de cada pieza, con el fin de observar la microfiltración alcanzada. La microfiltración se observó ...

Objetivo: Comparar, a las 48 horas, la microdureza superficial de las resinas para reconstrucción de muñones Luxa- core DMG America, Absolute Dentin Parkell y Z350 XT 3M. Materiales y métodos: El grupo de estudio estuvo conformado por 33 discos de resina, distribuidos en tres subgrupos: dos experimentales cada uno conformado por (n = 11), y uno control (n = 11). Los dos primeros grupos son resinas de foto activación y el tercero, una resina de activación dual. Estos fueron sometidos al instrumento microdurómetro Vickers, marca LG, en el laboratorio de ensayos mecánicos. Se aplicó una carga de 200 gramos fuerza por 10 segundos para cada indentación. El análisis estadístico se realizó con ayuda del programa SPSS versión 24 y se realizó la prueba de Anova y la prueba de comparación múltiple de Tukey. Resultados: Luego del ensayo de microdureza Vickers (VHN), los resul- tados...

El uso de las férulas oclusales en la actualidad, en el vasto campo de la odontología, es de gran importancia para el tratamiento de trastornos témporo mandibulares (TTM), así como en el tratamiento de otras para funciones relacionadas con la articulación témporo mandibular (ATM). Actualmente, existe variedad en cuanto al diseño de férulas oclusales, hechas con diferentes materiales, con diferentes resistencias y utilizadas para cada tipo de disfunción temporomandibular que se presente, así como para las parafunciones existentes. Dentro de esta variedad son solo cinco tipos de férulas las que se conocen ampliamente, según la evidencia científica. Cada una de ellas tiende a considerar diversas características en la forma de fabricación y sus indicaciones; así mismo, el clínico debe ejecutar una buena elección, un plan de control adecuado para cada caso, con un diagnósti...

The aim of this study is to compare in vitro the degree of marginal microleakage in pressed ceramic inlays made with two self-adhesive dual resin cements seT PP (SDI) and RelyX U200 (3M ESPE). Forty upper and lower premolars extracted for orthodontic reasons were evaluated and divided into two groups according to assigned cement (n = 20). Then, the preparation of class II type cavities, approximately 3 mm wide, was performed in the occlusal and proximal box; and 2 mm thick on the gingival floor and occlusal wall. They were indirectly restored with IPS e.max Press (Ivoclar Vivadent) ceramic pressed restorations, cemented with the types of cement studied according to the manufacturer's specifications. The specimens were kept in a jar and taken to thermocycling; then, cross sections were made to the crowns and the degree of microleakage was evaluated by means of a stereoscope. When comparin...

Tooth wear is the loss of hard tissue of multiple aetiology and may be due to functional or parafunctional factors. Depending on this, a restorative treatment should be chosen based on the severity of the wear, as it can result in loss of vertical dimension of occlusion (VOD), tooth sensitivity, and decreased quality of life. In these cases, the choice of restoration strategy must follow evidence-based treatment protocols, which include direct and indirect restoration techniques, as well as minimally invasive treatments based on composite resins that emerge as an alternative to conventional restorations of ceramics. This clinical case describes the treatment of a patient with severe dental wear through oral rehabilitation with composite resins through direct and indirect techniques, with the aim of preserving the tooth structure as much as possible and having greater aesthetic-functional...

The increasing demand of patients for esthetics dentistry treatments has led to the development of multidisciplinary communication between approaches among different specialties to achieve treatment success. The gummy smile is a frequent esthetic problem, which consists of excessive exposure of the gum when smiling. Treatment modalities range from gingivectomy to flap lift for the removal of excess bone. Restoration with direct veneers of composite resins is suitable for the preservation and esthetic improvement of the anterior sector, with optimal aesthetics and durability. In addition, minimally invasive treatment can be considered due to its conservative concepts of preserving the dental structure. The present case describes the treatment of a young patient with gummy smile and alteration in shape and color of the anterior teeth, through minimally invasive procedures such as gingivect...

Objective: To evaluate and compare the flexural strength of conventional flowable, bulk fill flowable and highly filled flowable resins. Materials and methods: Thirty 2mm x 2mm x 25mm specimens of Tetric N-Flow (TNF), Filtek Bulk Fill Flowable Restorative (FBF) and Beautifil Flow Plus F00 (BFP) flowable resins were made up; they were distributed into three groups according to brand (n=10) and stored in distilled water for 24 hours at 37ºC. The 3-point bending test according to ISO 4049 was performed on a universal testing machine at a speed of 0.5 mm/min until fracture. The results were evaluated with Anova and Tukey tests. P<0.05. Results: Statistically significant differences were found between the groups with a value of p=0.011. According to the statistical analysis, the groups that showed statistically significant differences were the BFP and TNF groups (p=0.015) and the BFP and ...

Evaluar el efecto del enjuague bucal Vitis CPC Protect en la microdureza superficial de tres tipos de polimetilmetacrilato (PMMA): autocurado (Alike), termocurado (Vitalloy) y CAD/ CAM (Telio CAD). Metodología: Se fabricaron 90 discos de PMMA, divididos en tres grupos de 30 discos, con dimensiones de 2 mm de espesor y 10 mm de diámetro. Cada grupo se subdividió en tres subgrupos (n = 10): el primero para medir la microdureza inicial, el segundo se sumergió en agua destilada como control, y el tercero en enjuague bucal Vitis CPC Protect. Los discos se mantuvieron en soluciones de 20 ml durante 6 horas a 37 °C, para simular el uso diario del enjuague dos veces al día durante 6 meses. La microdureza superficial Vickers se midió antes y después de la inmersión utilizando un durómetro Vickers con una carga de 50 g. Posteriormente, los datos fueron analizados estadísticamente median...