The work described in this paper was financially supported by the National Fund for the Scientific and Technological Development (FONDECYT), Grant No. 237–2015-FONDECYT. The authors thank Dr. Breno Pannia Espósito and the LABQAM of the Chemistry Institute of USP for the analysis of the samples. In addition, authors thank Dr. Pierre Ramos Apestegui for his excellent technical assistance with scanning electron microscopy observation.

MgCaSi2O6 polycrystal was synthesized by the devitrification method. The dosimetric characteristics by TL of this prepared polycrystal was investigated. This material exhibits TL peaks at 115, 160, 210, 260 and 280 °C. The dosimetric peak occurs at 260 °C with a well defined glow curve structure. This peak shows a linear dose response. Electron paramagnetic resonance (EPR) studies have been carried out to identify the defect centers responsible for the TL peaks. Two defect centers in the region of g = 2.0 are found. One of the centers (center I) with a g factor equal to 2.0085 is identified as O− -ion and relates with the observed high temperature 250 and 300 °C TL peaks. Additional defect centers with g = 2.0012 (center II) and 1.982 (center III) are due to F+- centers (electron trapped at an oxygen vacancy). Center II and III correlate with the TL peaks at 160 °C and 106 °C, res...