In this work, we study the synthesis process and structural and magnetic characterization of the ?-Al5Fe2 intermetallic alloy obtained by the arc-melting technique. Subsequently, in order to obtain homogeneous crystalline phase, all melted samples were annealed at 847?C during 2 days, and then quenched into water. The structural and micro-structural characterization of the samples were performed by X-ray diffraction and,57Fe transmission Mössbauer spectroscopy, while the morphological study was performed using scanning electron microscopy. Moreover, magnetic characterization was carried out using vibrating sample magnetometer. X-ray fluorescence was employed for elemental characterization. The results indicate that it is possible to employ the arc-melting technique to synthesize the ?-Al5Fe2 intermetallic phase with high structural quality: orthorhombic crystalline structure and Cmcm sp...

Se realiza el estudio de la síntesis y la influencia de la nano-estructuración sobre las propiedades estructurales, magnéticas y mecánicas del sistema intermetálico Al5Fe2 obtenido por la técnica de horno de arco y posterior tratamiento térmico, para finalmente ser nano-estructurado usando un molino vibratorio de alta energía. Las características morfológicas, micro-estructurales, estructurales, magnéticas y mecánicas de las muestras sintetizadas y nano-estructuradas fueron realizadas en los equipos de microscopía electrónica de barrido (MEB), fluorescencia de rayos X (FRX), difracción de rayos X (DRX), espectrosocpía Mössbauer de transmisión (EMT), magnetometría de muestra vibrante (MMV) y ensayo de dureza Vickers (HV). Los resultados de microscopía y difracción muestran que es posible obtener el sistema intermetálico con alta calidad estructural. Además, mediante...