The purpose of this work is to determine the influence of the carbon dioxide (CO2) gaseous curing method on the compressive strength of concrete for a design f'c =210 Kg/cm2. The research is of an applied nature of explanatory level and experimental design, in addition, the standards of the following Norms (NTP and ASTM) were used, with a sample of 32 specimens (16 samples cured with the traditional H2O method and 16 experimental samples cured with CO2, in gaseous state). In addition, the DCA and the T student test were used to test the hypotheses, and the Shapiro Wilk normality test was applied. For concrete cured with the traditional method, the average strength was 93 kg/cm² at 7 days, 141.27 kg/cm² at 14 days, 170.05 kg/cm² at 21 days, and 211.07 kg/cm² at 28 days. With CO2 curing, the resistance was 146.4 kg/cm² at 7 days, 195.39 kg/cm² at 14 days, 216.04 kg/cm² at 21 days, a...

El propósito o intención de este trabajo de investigación es aclarar la influencia del método de curado con di óxido de carbono (CO2) en estado gaseoso, en la resistencia a la compresión del concreto F’c =210 Kg/cm2 en la localidad de Huancavelica. La investigación es de naturaleza aplicada de nivel explicativo y de diseño experimental, además se utilizó los estándares de las siguientes Normas (NTP y ASTM), con una muestra de 32 testigos de concreto agrupados (16 muestras curadas con el método tradicional - agua y 16 muestras experimental curadas con el método de dióxido de carbono (CO2), en estado gaseoso). Además, para la comprobación de las hipótesis se utilizaron el DCA y la prueba T student, además se aplicó el test de normalidad de Shapiro Wilk. Para el objetivo específico 1 el valor de T (T crítica), con nivel de significancia de 5%, siendo el valor T críti...