Objective. To compare the hardness, dimensional stability, and compressive strength of high-strength, low-expansion dental plasters available in Peru, according to ADA criteria. Methods. A descriptive, observational and cross-sectional study was developed. A selection of 8 cylindrical-shaped samples and 8 rectangular- shaped ones, from seven high-resistance, low-expansion dental plasters were fabricated. The hardness was evaluated using the Identec Universal Durometer. Dimensional stability was evaluated with a digital caliper and compressive strength was evaluated with the Instron Universal Testing Machine. To determine if there is a difference in each of these properties, the analysis of variance, F test, and the Duncan’s test were used. In addition, to assess whether these values differ from those of the ADA, the mean comparison test, student’s t table, were used. Results. The har...

El presente trabajo compara la microfiltración apical de dos técnicas de Apicectomía, la Horizontal y la Oblicua, con obturación retrograda con Agregado Trióxido Mineral, siguiendo un diseño experimental y libre, para ello se usaron 17 premolares inferiores monorradiculares de reciente extracción para cada grupo de técnica de apicectomía; la microfiltración apical fue medida cuantitativamente por los indicadores; nivel 1 (0 a 1mm), nivel 2 (1 a 2mm) y nivel 3 (2 a mas). Los resultados obtenidos con la técnica de Apicectomía Horizontal fueron de 16 casos en el nivel 1 (0 a 1mm) y 01 caso en el nivel 2 (1 a 2mm). Mientras que para el grupo que se empleo la técnica de Apicectomía Oblicua se encontraron 01 casos en el nivel 1(0 a 1mm) y 16 caso en el nivel 2 (1 a 2mm). La microfiltración apical promedio para el grupo que se empleo la técnica de Apicectomía Horizontal fue de ...

ABSTRAC This research study, cross-sectional, observational and in vitro; was used to compare the tensile strength of two conventional AllCem (FGM) and Relyx Arc (3M) cements in Z350 (3M) composite resin inlays, using 17 seconds and upper and lower third molars free of caries of Recent extraction for each group; The tensile strength was measured quantitatively with the Instron 8801 universal test machine in Mpa with a speed of 2mm / min. The average tensile strength results obtained with conventional dual cement AllCem (FGM) were 22.75 ± 6.78 MPa. While for the conventional dual cement group Relyx Arc (3M) they were 24.44 ± 6.98 MPa. Thus, there was no significant difference (p> 0.05) between the tensile strength values in composite resin inlays with conventional AllCem (FGM) and Relyx Arc (3M) dual cement.

El estudio de investigación de tipo descriptivo, comparativo, observacional y de corte transversal tuvo como propósito determinar y comparar la dureza, resistencia a compresión y estabilidad dimensional de los yesos dentales tipo IV de mayor comercialización nacional, para lo cual se utilizaron 8 muestras de forma cilíndrica de cada yeso dental tipo IV para evaluar la dureza, y 8 muestras de forma rectangular para evaluar la resistencia a compresión y estabilidad dimensional. La dureza se evaluó con el Durómetro Universal Identec, realizando tres identaciones en cada muestra. La resistencia a compresión se evaluó con la máquina de ensayo universal Instron 8801 a una velocidad de 2 mm/min hasta que se fracture cada muestra; y la estabilidad dimensional se evaluó midiendo el volumen inicial y volumen final después de dos horas respectivamente de cada muestra. Los resultados ob...