Synthetic hydroxyapatite is a biomaterial widely used in guided bone regeneration procedures. Objective: Synthesize synthetic hydroxyapatite from eggshells under different precipitates of nitric acid. Methods: Experimental study, which obtained CaCO3 from the pulverization of eggshells (Gallus gallus). The carbonate was titrated with three concentrations of nitric acid (5, 10 and 15%) and ammonium phosphate. The mixtures were tested at different calcination temperatures (150, 600, 700, 800 and 900 °C) and calcination times (2, 4, 8 and 12 h). X-ray diffraction analysis was used to characterize the presence of calcium carbonate and hydroxyapatite. Results: Of the different routes of synthesis, the route of precipitation of nitric acid by excess to 15% plus calcined calcium carbonate at 700 °C during 8h offered more equivalent results to the synthetic hydroxyapatite when compared with th...

La hidroxiapatita sintética es un biomaterial ampliamente utilizado en los procedimientos de regeneración ósea guiada. Objetivo: Sintetizar hidroxiapatita sintética a partir de la cáscara de huevo bajo distintos precipitados de ácido nítrico. Métodos: Estudio experimental que obtuvo CaCO3 a partir de la pulverización de la cáscara de huevo (Gallus gallus). El carbonato fue titulado con tres concentraciones de ácido nítrico (5, 10 y 15%) y fosfato de amonio. De las mezclas se realizaron pruebas a distintas temperaturas de calcinación (150, 600, 700, 800 y 900 °C) y tiempos de calcinación (2, 4, 8 y 12 h). Se utilizó el análisis de difracción de rayos X para caracterizar la presencia de carbonato de calcio e hidroxiapatita. Resultados: De las distintas rutas de síntesis, la vía de precipitación de ácido nítrico por exceso al 15% más el carbonato de calcio calcinado ...