Cultural heritage materials are affected by diverse environmental agents such as humidity, temperature, and pollution. This work focuses on studying the thermodynamic stability of Peruvian heritage materials such as gilded coppers and pigments within two scenarios: one under ambient conditions and the other under accelerated conditions established by the ASTM D 2247 standard. In both cases, the HSC Chemistry 6 software was implemented. The general results obtained for gilded coppers showed that by varying the relative humidity from 75% and 14 °C to 80% and 26 °C, the corrosion products move from CuO to Cu(OH) 2. In addition, to Cu2Cl(OH)3-Atacamite-in the presence of chlorin. On the other hand, for hematite (Fe 3O 2), vermilion (HgS), and Minium (Pb 3O 4) pigments, we found that at ambient conditions, with NO 2 and SO 2, they give rise to goethite (FeO(OH)), mercury sulfate (HgSO 4) an...