Sugarcane bagasse ash in the compressive strength of concrete

• Autores: Farfán Córdova, Marlon Gastón, Pastor Simón, Hary Hernando
• Formato: artículo
• Fecha de Publicación: 2019
• Institución: Universidad César Vallejo
• Repositorio: Revista UCV-HACER
• Lenguaje: español
• OAI Identifier: oai:ojs.pkp.sfu.ca:article/1791
• Enlace del recurso: http://revistas.ucv.edu.pe/index.php/UCV-HACER/article/view/1791
• Nivel de acceso: acceso abierto

In this investigation, the effect of sugarcane bagasse ash (SBA) on concrete strength of 210 kg/cm2 is evaluated, partially replacing SBA with cement, in proportions of 20 and 40%. The results showed that the compressive strength of the concrete decreased with increasing ash content, below the design mix. Concrete with 20% SBA had better compressive performance at 7 and 28 days of cure, although both were 59% below standard concrete (control). This suggests not recommending SBA for structural use because of its decreased compressive strength.   Keywords: agro-industrial waste, concrete, sugarcane bagasse.  
En esta investigación se evalúa el efecto de la ceniza de caña de azúcar (CBCA) en la resistencia del concreto de 210 kg/cm2, reemplazando parcialmente CBCA por el cemento, en proporciones de 20 y 40%. Los resultados mostraron que la resistencia a la compresión del concreto disminuyó con el incremento de la proporción de ceniza, por debajo de la mezcla de diseño. El concreto con 20% de CBCA tuvo mejor comportamiento a compresión a los 7 y 28 días de curado, aunque ambas estuvieron 59% por debajo del concreto estándar (control). Esto sugiere no recomendar la CBCA para el uso estructural por su disminuida resistencia a la compresión.   Palabras clave: residuos agroindustriales, concreto, bagazo de caña de azúcar.