In this paper we present a systematic study of the thickness dependence of the magnetic properties of disordered FCC-FePt thin films. Films with thicknesses between 9 nm and 94 nm were prepared by DC magnetron sputtering technique and deposited on naturally oxidized Si (100) substrates at room temperature. X ray diffraction measurements show that the films grow with a texture along the [111] direction, perpendicular to the film plane, and that they are under in-plane planar compressive stress. In-plane magnetic hysteresis loops show that there is a critical thickness of approximately 30 nm above which a significant change of the magnetic domain structure is observed. Thinner films (9 nm ≤ t ≤ 28 nm) show an in-plane uniaxial anisotropy characterized by a square hysteresis loop, while thicker films (35 nm ≤ t ≤ 94 nm) show a magnetization reversal in a two steps process, which is ...

Debido al aumento de los costos operativos y los prolongados tiempos de retorno de inversión, la industria minera busca optimizar continuamente sus procesos de beneficio. Este estudio presenta una metodología basada en el Proyecto Internacional AMIRA P9, que emplea herramientas de modelamiento y simulación como Bruno, JKSimMet y Limn® para evaluar y mejorar la eficiencia operativa con mínima inversión y riesgo. La metodología se compone de las siguientes etapas: extracción de información del proceso, análisis de datos, elaboración de balances metalúrgicos, evaluación del rendimiento de los equipos, modelamiento y ajuste de parámetros, y ejecución de simulaciones. Como resultado de la aplicación de la metodología en una unidad de Sierra Metals Inc. ubicada al norte de México, en el circuito de trituración, se determinó que la trituradora primaria 20' x 36' puede operar...